An analysis of the internal oxidation of binary M-Nb alloys under low oxygen pressures at 600-800{degrees}C
- Universita di Genova (Italy)
- Institute of Corrosion and Protection of Metals, Shenyang (China); and others
The corrosion of M-Nb alloys based on iron, cobalt, and nickel and containing 15 and 30 wt% Nb has been studied at 600-800{degrees}C under low oxygen pressures (10{sup {minus}24} atm at 600{degrees}C and 10{sup {minus}20} atm at 700-800{degrees}C). Except for the Co-Nb and Ni-Nb alloys corroded at 800{degrees}C, which formed external scales of niobium oxides, corrosion under low O{sub 2} pressures produced an internal oxidation of niobium. This attack was much faster than expected on the basis of the classical theory. Furthermore, the distribution of the internal oxide in the alloys containing two metal phases was very close to that of the Nb-rich phase in the original alloys. These kinetic, microstructural, and thermodynamic aspects are examined by taking into account the effects of the limited solubility of niobium in the various base metals and of the two-phase nature of the alloys.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 482501
- Journal Information:
- Oxidation of Metals, Journal Name: Oxidation of Metals Journal Issue: 5-6 Vol. 46; ISSN OXMEAF; ISSN 0030-770X
- Country of Publication:
- United States
- Language:
- English
Similar Records
The oxidation of Co-Nb alloys under low oxygen pressures at 600-800{degrees}C
The oxidation of two Fe-Nb alloys under low oxygen pressures at 600-800{degrees}C