Effect of oxygen partial pressure on superconducting properties of Bi-2212/Ag tapes prepared by doctor-blade method
- Hitachi Research Lab. (Japan); and others
The authors have investigated the relationship between oxygen partial pressure (P{sub O{sub 2}}) during the partial-melting process and superconducting properties for doctor-blade processed Bi-2212/Ag tapes. Tapes were heat-treated at various P{sub O{sub 2}} value of 0.01-1.00 atm. The DTA results for the doctor-blade tapes showed the melting point of the oxide rose with increasing P{sub O{sub 2}}. Correspondingly, the optimum heat-treatment temperature also increased with increasing P{sub O{sub 2}}. The tapes at P{sub O{sub 2}}=1.00 atm had the highest J{sub c} values of over 10{sup 5} A/cm{sup 2} at conditions of 4.2K, 10T, and their a.c. susceptibility showed a sharp transition indicating improved intergrain coupling. Examination of cross sections for tapes melted above 0.20atm PO{sub 2} showed the good crystal alignment. From these results, it was concluded that processing at high PO{sub 2} was an effective method to obtain good superconducting properties for doctor-blade tapes.
- OSTI ID:
- 482095
- Report Number(s):
- CONF-950722-; ISSN 0065-2482; TRN: 97:001732-0046
- Journal Information:
- Advances in Cryogenic Engineering, Vol. 42B; Conference: CEC/ICMC `95: cryogenic engineering conference and international cryogenic materials conference, Columbus, OH (United States), 17-21 Jul 1995; Other Information: PBD: 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
The role of silver in the processing and properties of Bi-2212
Tape casting and partial melting of Bi-2212 thick films