INVESTIGATIONS OF TIN BASE Sn-Ti ALLOYS (in Russian)
Journal Article
·
· Zh. Neorgan. Khim.
OSTI ID:4769536
The structure and properties of tin with 0 to 20 wt.% Ti were studied. The addition of Ti reduces the crystallization temperature. The diffusion of Ti in Sn solid solution is very low, 0.008 to 0.008 wt.% Ti. A non-variant transformation takes place in alloys containing 8.3 to 34.8 wt.% Ti at 790 deg C. The nature of the transformation was not determined. (R.V.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-17-001992
- OSTI ID:
- 4769536
- Journal Information:
- Zh. Neorgan. Khim., Journal Name: Zh. Neorgan. Khim. Vol. Vol: 7
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
STRUCTURE AND PROPERTIES OF NIOBIUM-TIN ALLOYS
CONTINUOUS SOLID SOLUTIONS OF THE INTERMETALLICS Ti$sub 3$Al AND Ti$sub 3$Sn IN THE Ti-Al-Sn SYSTEM
INVARIABLE TRANSFORMATIONS IN Al-Ti ALLOYS
Journal Article
·
Tue Sep 01 00:00:00 EDT 1959
· Izvest. Akad. Nauk S.S.S.R., Otdel. Tekh. Nauk, Met. i Toplivo
·
OSTI ID:4175236
CONTINUOUS SOLID SOLUTIONS OF THE INTERMETALLICS Ti$sub 3$Al AND Ti$sub 3$Sn IN THE Ti-Al-Sn SYSTEM
Journal Article
·
Sun Oct 01 00:00:00 EDT 1961
· Doklady Akad. Nauk S.S.S.R.
·
OSTI ID:4816855
INVARIABLE TRANSFORMATIONS IN Al-Ti ALLOYS
Journal Article
·
Thu Aug 01 00:00:00 EDT 1957
· Izvest. Akad. Nauk S.S.S.R. Otdel. Tekh. Nauk
·
OSTI ID:4330460