STRESS-CORROSION CRACKING OF 17-4 PH STAINLESS STEEL
Technical Report
·
OSTI ID:4765090
Exposure of 17-4 PH stainless steel to a simulated HWCTR environment indicates that this alloy is susceptible to stress-corrosion cracking when aged at 900 deg F, but is not susceptible when aged at 1100 deg F. (auth)
- Research Organization:
- Du Pont de Nemours (E.I.) & Co. Savannah River Lab., Aiken, S.C.
- DOE Contract Number:
- AT(07-2)-1
- NSA Number:
- NSA-16-033429
- OSTI ID:
- 4765090
- Report Number(s):
- DP-779
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-62
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of pH on stress corrosion cracking of 18-8 stainless steel in low-chloride water
Stress-Corrosion Cracking of Type 347 Stainless Steel And Other Alloys in High Temperature Water
Use of electrochemical potential noise to detect initiation and propagation of stress corrosion cracks in a 17-4 PH steel
Conference
·
Thu Mar 05 00:00:00 EST 1964
·
OSTI ID:4765090
Stress-Corrosion Cracking of Type 347 Stainless Steel And Other Alloys in High Temperature Water
Journal Article
·
Tue Oct 01 00:00:00 EDT 1963
· Corrosion (Houston)
·
OSTI ID:4765090
Use of electrochemical potential noise to detect initiation and propagation of stress corrosion cracks in a 17-4 PH steel
Journal Article
·
Mon Sep 01 00:00:00 EDT 1997
· Corrosion
·
OSTI ID:4765090
+1 more