FAILURE MODES OF ZIRCALOY-CLAD FUEL RODS. PART 3. DESCRIPTION OF THE ORNL PROGRAM.
Technical Report
·
OSTI ID:4721763
- Research Organization:
- Oak Ridge National Lab., Tenn.
- DOE Contract Number:
- W-7405-ENG-26
- NSA Number:
- NSA-24-009106
- OSTI ID:
- 4721763
- Report Number(s):
- ORNL-TM--2742
- Country of Publication:
- United States
- Language:
- English
Similar Records
FAILURE MODES OF ZIRCALOY-CLAD FUEL RODS. PART 2. PROGRAM REVISIONS.
FAILURE MODES OF ZIRCALOY-CLAD FUEL RODS.
EFFECT OF IRRADIATION ON THE FAILURE OF ZIRCALOY-CLAD FUEL RODS.
Technical Report
·
Tue Dec 31 23:00:00 EST 1968
·
OSTI ID:4779345
FAILURE MODES OF ZIRCALOY-CLAD FUEL RODS.
Technical Report
·
Sun Dec 31 23:00:00 EST 1967
·
OSTI ID:4494557
EFFECT OF IRRADIATION ON THE FAILURE OF ZIRCALOY-CLAD FUEL RODS.
Technical Report
·
Fri Dec 31 23:00:00 EST 1971
·
OSTI ID:4708138
Related Subjects
ACCIDENTS
FAILURES
FUEL CANS
LOSSES
MECHANICAL PROPERTIES
N38150* --Power Reactor Development--Fuels
N38180 --Power Reactor Development--Safety & Siting
REACTOR FUEL ELEMENTS/failure of Zircaloy clad
in water cooled reactor coolant loss accidents
REACTOR SAFETY
REACTORS
WATER-COOLED/coolant loss accidents in
effect on Zircaloy clad fuel rod failure of
STEAM/effects on embrittlement of Zircaloy cladding of reactor fuel elements
WATER COOLANT
WATER COOLED REACTORS
ZIRCALOY
ZIRCALOY/failure of reactor fuel element cladding of
effects of coolant loss accidents on
ZIRCALOY/mechanical properties at high temperatures
FAILURES
FUEL CANS
LOSSES
MECHANICAL PROPERTIES
N38150* --Power Reactor Development--Fuels
N38180 --Power Reactor Development--Safety & Siting
REACTOR FUEL ELEMENTS/failure of Zircaloy clad
in water cooled reactor coolant loss accidents
REACTOR SAFETY
REACTORS
WATER-COOLED/coolant loss accidents in
effect on Zircaloy clad fuel rod failure of
STEAM/effects on embrittlement of Zircaloy cladding of reactor fuel elements
WATER COOLANT
WATER COOLED REACTORS
ZIRCALOY
ZIRCALOY/failure of reactor fuel element cladding of
effects of coolant loss accidents on
ZIRCALOY/mechanical properties at high temperatures