INCREASED LIFETIME OF GRAPHITES IRRADIATED ABOVE 1200$sup 0$C.
Journal Article
·
· Carbon 9: No. 6, 699-710(Dec 1971).
- Research Organization:
- Battelle-Northwest, Richland, Wash.
- NSA Number:
- NSA-26-012799
- OSTI ID:
- 4700424
- Journal Information:
- Carbon 9: No. 6, 699-710(Dec 1971)., Journal Name: Carbon 9: No. 6, 699-710(Dec 1971).
- Country of Publication:
- United Kingdom
- Language:
- English
Similar Records
GRAPHITE IRRADIATIONS 300$sup 0$ TO 1200$sup 0$C.
IRRADIATION OF GRAPHITE AT TEMPERATURES OF 300 TO 1200$sup 0$C.
IRRADIATION OF GRAPHITE AT TEMPERATURES OF 300 TO 1200 $sup 0$C.
Journal Article
·
Tue Dec 31 23:00:00 EST 1968
· Carbon, 7: 319-27(Apr. 1969).
·
OSTI ID:4794849
IRRADIATION OF GRAPHITE AT TEMPERATURES OF 300 TO 1200$sup 0$C.
Technical Report
·
Tue Dec 31 23:00:00 EST 1968
·
OSTI ID:4778830
IRRADIATION OF GRAPHITE AT TEMPERATURES OF 300 TO 1200 $sup 0$C.
Technical Report
·
Tue Dec 31 23:00:00 EST 1968
·
OSTI ID:4749558
Related Subjects
ANNEALING
CONTRACTION
CREEP
CRYSTALS
DEFORMATION
ELECTRIC CONDUCTIVITY
EXPANSION
FRACTURES
GRAPHITE
GRAPHITE/radiation effects on dimensional stability above 1200$sup 0$C
fast neutron
HIGH TEMPERATURE
IRRADIATION
N30250* --Metals
Ceramics
& Other Materials--Ceramics & Cermets--Radiation Effects
NEUTRON FLUX
NEUTRONS
FAST/effects on dimensional stability of graphite above 1200--C
RADIATION EFFECTS
STRAIN
CONTRACTION
CREEP
CRYSTALS
DEFORMATION
ELECTRIC CONDUCTIVITY
EXPANSION
FRACTURES
GRAPHITE
GRAPHITE/radiation effects on dimensional stability above 1200$sup 0$C
fast neutron
HIGH TEMPERATURE
IRRADIATION
N30250* --Metals
Ceramics
& Other Materials--Ceramics & Cermets--Radiation Effects
NEUTRON FLUX
NEUTRONS
FAST/effects on dimensional stability of graphite above 1200--C
RADIATION EFFECTS
STRAIN