THERMOMECHANICAL STRENGTHENING OF A $gamma$' PRECIPITATION-HARDENED NICKEL- BASE ALLOY.
Journal Article
·
· Met. Trans. 3: No. 3, 617-26(mar 1972).
- Research Organization:
- Pratt and Whitney Aircraft, Middletown, Conn.
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-26-023312
- OSTI ID:
- 4700296
- Journal Information:
- Met. Trans. 3: No. 3, 617-26(mar 1972)., Journal Name: Met. Trans. 3: No. 3, 617-26(mar 1972).; ISSN MTGTB
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
STRENGTHENING MECHANISMS IN $gamma$' HARDENED NICKEL BASE ALLOYS.
SUBSTRUCTURAL STRENGTHENING OF A PRECIPITATION-HARDENED MOLYBDENUM ALLOY.
THE MECHANISM OF CREEP IN GAMMA PRIME PRECIPITATION-HARDENED NICKEL-BASE ALLOYS AT INTERMEDIATE TEMPERATURES.
Journal Article
·
Thu Dec 31 23:00:00 EST 1970
· Scr. Met. 5: No. 11, 959-64(Nov 1971).
·
OSTI ID:4707572
SUBSTRUCTURAL STRENGTHENING OF A PRECIPITATION-HARDENED MOLYBDENUM ALLOY.
Journal Article
·
Sat Dec 31 23:00:00 EST 1966
· Acta Met., 15: 601-6(Apr. 1967).
·
OSTI ID:4439997
THE MECHANISM OF CREEP IN GAMMA PRIME PRECIPITATION-HARDENED NICKEL-BASE ALLOYS AT INTERMEDIATE TEMPERATURES.
Journal Article
·
Wed Dec 31 23:00:00 EST 1969
· Met. Trans. 1: 491-8(Feb 1970).
·
OSTI ID:4750512
Related Subjects
HEAT TREATMENTS
HIGH TEMPERATURE
MEDIUM TEMPERATURE
N50220* --Metals
Ceramics
& Other Materials--Metals & Alloys--Preparation & Fabrication
N50230 --Metals
Ceramics
& Other Materials--Metals & Alloys--Properties
Structure & Phase Studies
PRECIPITATION HARDENING
TENSILE PROPERTIES
UDIMET
UDIMET 700/strengthening of $gamma$' precipitation- hardened
at room temperature to 1400$sup 0$F
thermomechanical method for
VERY HIGH TEMPERATURE
HIGH TEMPERATURE
MEDIUM TEMPERATURE
N50220* --Metals
Ceramics
& Other Materials--Metals & Alloys--Preparation & Fabrication
N50230 --Metals
Ceramics
& Other Materials--Metals & Alloys--Properties
Structure & Phase Studies
PRECIPITATION HARDENING
TENSILE PROPERTIES
UDIMET
UDIMET 700/strengthening of $gamma$' precipitation- hardened
at room temperature to 1400$sup 0$F
thermomechanical method for
VERY HIGH TEMPERATURE