Environmental microscopy of capillary stress-induced strain behavior in ambinent-pressure aerogels
- Sandia National Labs., Albuquerque, NM (United States)
- Univ. of Minnesota, Minneapolis, MN (United States)
Ambient pressure silica aerogel thin films have recently been prepared by exploiting reversible drying shrinkage caused by derivatization of the internal gel surface. Aerogels have porosities of upto 99.9% and due to the small size of the pores (few nanometers), large capillary stresses are produced in gels that are partially saturated with a wetting liquid. As a result of these capillary stresses, the flexible silica network undergoes strain which has been observed using environmental microscopy. This technique allows variation of the equilibrium vapor pressure and temperature, and a simultaneous monitoring of the deformation during the pore-filling and pore-emptying cycles. In this presentation, we discuss the unique stress-strain behavior of these films.
- OSTI ID:
- 468923
- Report Number(s):
- CONF-960877-; TRN: 97:001308-0181
- Resource Relation:
- Conference: Microscopy and microanalysis 1996, Minneapolis, MN (United States), 11-15 Aug 1996; Other Information: PBD: 1996; Related Information: Is Part Of Microscopy and microanalysis 1996; Bailey, G.W.; Corbett, J.M.; Dimlich, R.V.W.; Michael, J.R.; Zaluzec, N.J. [eds.]; PB: 1107 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Transparent silica aerogel slabs synthesized from nanoparticle colloidal suspensions at near ambient conditions on omniphobic liquid substrates
A one-dimensional analysis of sol-gel film-coating drying: Pore evolution, network shrinkage and stress development