SHEAR STRENGTH PROPERTIES OF REFRACTORY METAL FASTENERS. Report 9346. Final Report
Technical Report
·
OSTI ID:4662575
Ultimate shear strength tests were conducted in air at ruom temperature and 1600 deg F. Testing was performed on five refractory alloys: (Cb-10Ti-10W, Cb- 10Ti-3Zr). Mo-0,5Ti, Cb-1Zr, Cb-15W-5Mo-1Zr (F48); and seven types of fasteners; solid rivets, explosive rivets, Crcoated rivets, Huck rivets, Deutsch rivets, DuPont explosive rivets, and solid bolts. The F-48 solid rivets both at room temperature and at 1600 deg F (87,000 psi and 54,500 psi). Data are ph form. (auth)
- Research Organization:
- McDonnell Aircraft Corp., St. Louis
- NSA Number:
- NSA-17-036281
- OSTI ID:
- 4662575
- Report Number(s):
- AD-295526
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY FORGINGS. Interim Technical Engineering Report, December 15, 1960-March 15, 1961
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY FORGINGS. Interim Technical Engineering Report, March 15, 1961-August 15, 1961
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Progress Report, September 15, 1960-December 15, 1960
Technical Report
·
Tue Feb 28 23:00:00 EST 1961
·
OSTI ID:4031978
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY FORGINGS. Interim Technical Engineering Report, March 15, 1961-August 15, 1961
Technical Report
·
Tue Aug 01 00:00:00 EDT 1961
·
OSTI ID:4841706
THE DEVELOPMENT OF OPTIMUM MANUFACTURING METHODS FOR COLUMBIUM ALLOY SHEET. Interim Technical Progress Report, September 15, 1960-December 15, 1960
Technical Report
·
Wed Nov 30 23:00:00 EST 1960
·
OSTI ID:4045375