THORIA-DISPERSED NICKEL NEW ALLOY FOR HOT JOBS
Journal Article
·
· Prod. Eng.
OSTI ID:4661061
S>A comparison was made of thoria dispersed Ni with Haynes 25 alloy, SM 302, Hastelloy X, and Rene 4l in terms of oxidation and corrosion resistance, stress rupture strength, rupture life, and high temperature tensile strength. (Rev. Metal Lit., 19: No. 10, Oct. 1962)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-17-032501
- OSTI ID:
- 4661061
- Journal Information:
- Prod. Eng., Journal Name: Prod. Eng. Vol. Vol: 33
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
WESTINGHOUSE ALLOY B 33 (HIGH TEMPERATURE COLUMBIUM ALLOY)
HAYNES ALLOY Cb-752 (HIGH TEMPERATURE ALLOY)
SOME OBSERVATIONS ON THE COLD-DRAWING AND ANNEALING BEHAVIOUR OF NICKEL CONTAINING A DISPERSED PHASE OF THORIA
Journal Article
·
Tue Aug 01 00:00:00 EDT 1961
· Alloy Digest Cb-1
·
OSTI ID:4678953
HAYNES ALLOY Cb-752 (HIGH TEMPERATURE ALLOY)
Journal Article
·
Thu Oct 31 23:00:00 EST 1963
· Alloy Digest (U.S.)
·
OSTI ID:4085133
SOME OBSERVATIONS ON THE COLD-DRAWING AND ANNEALING BEHAVIOUR OF NICKEL CONTAINING A DISPERSED PHASE OF THORIA
Journal Article
·
Sun Dec 31 23:00:00 EST 1961
· Powder Met.
·
OSTI ID:4776638