Influence of yttria content on the preparation of nanocrystalline yttria-doped zirconia
- Institute for Self-Propagating High-Temperature Synthesis, New York State College of Ceramics at Alfred University, Alfred, New York, 14802 (United States)
Nanocrystalline zirconia doped with 0--10 mol % Y{sub 2}O{sub 3} has been prepared by a combustion synthesis process, followed by a rapid densification process. The concentration of Y{sub 2}O{sub 3} in the as-reacted zirconia appeared to have a significant influence on the reduction of the crystallite size, in the combustion temperature range studied (450 {degree}C--550 {degree}C), as well as on the stabilization of the tetragonal and/or cubic phases. The green compacts were densified by a fast-firing process. During fast-firing, the dwell temperature significantly affected the final average grain size and the final density of the article. On the other hand, the ranges of heating rates and dwell times that were used in this study were shown to have a much less significant effect on the article`s final density and final average grain size. The yttria content had the largest influence on the final density and final average grain size. The densification took place much more rapidly in the 4 mol % Y{sub 2}O{sub 3}--ZrO{sub 2} samples than in the 10 mol % Y{sub 2}O{sub 3}--ZrO{sub 2} samples. In particular, the difference in densification rates between the samples with different Y{sub 2}O{sub 3} content was attributed to the influence and magnitude of the associated grain-growth process. It was determined, however, that a high final density ({gt}99% {rho}{sub th}) and a very fine final average grain size ({lt}200 nm) could be simultaneously achieved with each of three different heating rates for the 4 mol % Y{sub 2}O{sub 3}--ZrO{sub 2} articles.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FG02-93ER12128
- OSTI ID:
- 46339
- Journal Information:
- Journal of Materials Research, Vol. 10, Issue 3; Other Information: PBD: Mar 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Rapid rate sintering of nanocrystalline ZrO{sub 2}-3 mol% Y{sub 2}O{sub 3}
Electrical properties of ultrafine-grained yttria-stabilized zirconia ceramics