OSTI ID:460778
Residual stress distribution in a HY-100 steel disk, induced by GTA spot welding, was analyzed by finite element (FE) formulations and measured by neutron diffraction (ND). Computations used temperature- dependent thermophysical and mechanical properties. FE model predictions are in good agreement with ND data in far heat affected zone (HAZ) and in base metal. Predicted residual stresses in fusion zone and near HAZ were higher than those measured by ND. This discrepancy was attributed to microstructural changes and associated material properties in the HAZ and fusion zone due to phase transformations during the weld thermal cycle.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Research, Washington, DC (United States); Office of Naval Research, Washington, DC (United States)
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 460778
- Report Number(s):
- CONF-970558--2; ON: DE97002631; CNN: Agreement No. 1866-E126-A1
- Country of Publication:
- United States
- Language:
- English
Similar Records
Modeling and validation of residual stress distribution in an HSLA-100 disk
Evaluation of flow properties in the weldments of vanadium alloys using a novel indentation technique
Effects of residual stresses and distortion on the nickel 200 and stainless steel 304 weldments
Conference
·
Sat Dec 30 23:00:00 EST 1995
·
OSTI ID:204181
Evaluation of flow properties in the weldments of vanadium alloys using a novel indentation technique
Technical Report
·
Tue Oct 01 00:00:00 EDT 1996
·
OSTI ID:414857
Effects of residual stresses and distortion on the nickel 200 and stainless steel 304 weldments
Technical Report
·
Wed Sep 26 00:00:00 EDT 1984
·
OSTI ID:5840951