Properties of LiCoO{sub 2}-coated NiO MCFC cathode
- Korea Univ., Seoul (Korea, Republic of)
- Samsung Electronics Co. Ltd., Suwon (Korea, Republic of)
PVA-assisted sol-gel method is useful in producing metal oxides with large surface area at low temperature. We fabricated LiCoO{sub 2}-coated NiO(LC-NiO) cathode by PVA-assisted sol-gel method and measured its properties, The electrical conductivity of LC-NiO cathode was measured to be more than 5 times as high as that of NiO and unit cell test showed improved performance. From the SEM images and Raman spectra. we confirmed that the structure of LC-NiO was different from that of NiO. For 250 hours of steady operation of unit cells. the mean voltage of the cells were 0.78V for NiO and 0.85V for LiCoO{sub 2}-Coated NiO at a current density of l50mA/cm{sup 2}.
- Research Organization:
- Fuel Cell Seminar Organizing Committee (United States)
- OSTI ID:
- 460242
- Report Number(s):
- CONF-961107--Absts.; ON: TI97001494
- Country of Publication:
- United States
- Language:
- English
Similar Records
The development of LiFeO{sub 2}-LiCoO{sub 2}-NiO cathodes for molten carbonate fuel cells
OPTIMIZATION OF THE CATHODE LONG-TERM STABILITY IN MOLTEN CARBONATE FUEL CELLS: EXPERIMENTAL STUDY AND MATHEMATICAL MODELING
Improving thermal and electrochemical performances of LiCoO{sub 2} cathode at high cut-off charge potentials by MF{sub 3} (M=Ce, Al) coating
Journal Article
·
Wed Mar 31 23:00:00 EST 1999
· Journal of the Electrochemical Society
·
OSTI ID:345320
OPTIMIZATION OF THE CATHODE LONG-TERM STABILITY IN MOLTEN CARBONATE FUEL CELLS: EXPERIMENTAL STUDY AND MATHEMATICAL MODELING
Technical Report
·
Mon Oct 01 00:00:00 EDT 2001
·
OSTI ID:808971
Improving thermal and electrochemical performances of LiCoO{sub 2} cathode at high cut-off charge potentials by MF{sub 3} (M=Ce, Al) coating
Journal Article
·
Thu Jan 14 23:00:00 EST 2016
· Materials Research Bulletin
·
OSTI ID:22584274