Formation of lithium-cobalt spinel oxide (Li{sub x}Co{sub 3{minus}x}O{sub 4}) by solid-state reaction of a Li{sub 2}CO{sub 3}-Co{sub 3}O{sub 4} powder mixture
Journal Article
·
· Materials Research Bulletin
- ENEA C.R.E. Casaccia, Santa Maria di Galeria (Italy)
The formation of mixed lithium-cobalt spinel oxide Li{sub x}Co{sub 3{minus}x}O{sub 4} by solid-state reaction in air at low temperature between Li{sub 2}CO{sub 3} and Co{sub 3}O{sub 4} in the atomic ratio Li/Co 1.0 has been investigated by DTG, DTA, and X-ray diffraction measurements. Lithiated Co{sub 3}O{sub 4} was formed around 220 C. As at this temperature the diffusion rate of lithium ions into Co{sub 3}O{sub 4} lattice is very low, it can be assumed that only the surface of Co{sub 3}O{sub 4} particles was lithiated. By increasing the temperature above 380 C, LiCoO{sub 2} formation occurred.
- OSTI ID:
- 455220
- Journal Information:
- Materials Research Bulletin, Journal Name: Materials Research Bulletin Journal Issue: 1 Vol. 32; ISSN MRBUAC; ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
First-Principles Study of Lithium Cobalt Spinel Oxides: Correlating Structure and Electrochemistry
Solid-state CO{sub 2} sensor with Li{sub 2}CO{sub 3}-Li{sub 3}PO{sub 4}-LiAlO{sub 2} electrolyte and LiCoO{sub 2}-Co{sub 3}O{sub 4} as solid reference electrode
Synthesis and phase transition of Li-Mn-O spinels with high Li/Mn ratio by thermo-decomposition of LiMnC{sub 2}O{sub 4}(Ac)
Journal Article
·
Tue Apr 03 20:00:00 EDT 2018
· ACS Applied Materials and Interfaces
·
OSTI ID:1461501
Solid-state CO{sub 2} sensor with Li{sub 2}CO{sub 3}-Li{sub 3}PO{sub 4}-LiAlO{sub 2} electrolyte and LiCoO{sub 2}-Co{sub 3}O{sub 4} as solid reference electrode
Journal Article
·
Sun Nov 30 23:00:00 EST 1997
· Journal of the Electrochemical Society
·
OSTI ID:603757
Synthesis and phase transition of Li-Mn-O spinels with high Li/Mn ratio by thermo-decomposition of LiMnC{sub 2}O{sub 4}(Ac)
Journal Article
·
Sat Apr 15 00:00:00 EDT 2006
· Journal of Solid State Chemistry
·
OSTI ID:20784962