Tape casting of lanthanum chromite
- Pacific Northwest National Lab., Richland, WA (United States)
Solid oxide fuel cells (SOFCs) are currently being developed for a variety of applications such as stationary on-site power plants and cogeneration. The effects of process additives, ball milling, and solids loading were evaluated for tape casting suspensions of glycine-nitrate-synthesized La{sub 0.7}Ca{sub 0.31}CrO{sub 3} powder. An optimized formulation was obtained based on rheological characterization, electrokinetic sonic amplitude measurements, qualitative examination of green tapes, and the sintered microstructure. The tape casting formulation incorporated 66:34 methyl ethyl ketone/ethyl alcohol solvent, an aliphatic phosphate ester dispersant, and 80 wt% (35 vol%) solids. The best binder/plasticizer system was 12 wt% (15 vol%) poly(isobutyl methacrylate) and 5 wt% (6.3 vol%) benzyl butyl phthalate plasticizer (binder:plasticizer = 2.3). Cast tapes were sintered at 1300 C for 2 h, producing a bulk density of 96.2% theoretical, with linear shrinkage of 22% and an approximate grain size of 1.3 {micro}m.
- Sponsoring Organization:
- USDOE Morgantown Energy Technology Center, WV (United States); Gas Research Inst., Chicago, IL (United States)
- OSTI ID:
- 455167
- Journal Information:
- Journal of the American Ceramic Society, Vol. 80, Issue 1; Other Information: PBD: Jan 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tape casting of fine alumina/zirconia powders for composite fabrication
Low-temperature sintering and phase changes in chromite interconnect materials