BIAXIAL STRESS-RUPTURE PROPERTIES OF AUSTENITIC STAINLESS STEELS IN STATIC SODIUM.
- Research Organization:
- North American Aviation, Inc., Canoga Park, CA (United States). Atomics International Div.
- DOE Contract Number:
- AT(04-3)-701
- NSA Number:
- NSA-22-041032
- OSTI ID:
- 4508059
- Report Number(s):
- AI-AEC-12694
- Resource Relation:
- Other Information: UNCL. Orig. Receipt Date: 31-DEC-68
- Country of Publication:
- United States
- Language:
- English
Similar Records
BIAXIAL STRESS-RUPTURE PROPERTIES OF AUSTENITIC STAINLESS STEELS IN ZIRCONIUM-GETTERED SODIUM.
STRESS-RUPTURE BEHAVIOR OF TYPES 304 AND 316 STAINLESS STEEL CLADDING IN HIGH-TEMPERATURE STATIC SODIUM.
BIAXIAL CREEP AND STRESS RUPTURE OF WIRE-WRAPPED CLADDING IN 1200$sup 0$F SODIUM UNDER $delta$ T CONDITIONS. Interim Report.
Technical Report
·
Sun Jan 01 00:00:00 EST 1967
·
OSTI ID:4508059
STRESS-RUPTURE BEHAVIOR OF TYPES 304 AND 316 STAINLESS STEEL CLADDING IN HIGH-TEMPERATURE STATIC SODIUM.
Technical Report
·
Thu Jan 01 00:00:00 EST 1970
·
OSTI ID:4508059
BIAXIAL CREEP AND STRESS RUPTURE OF WIRE-WRAPPED CLADDING IN 1200$sup 0$F SODIUM UNDER $delta$ T CONDITIONS. Interim Report.
Technical Report
·
Thu Jan 01 00:00:00 EST 1970
·
OSTI ID:4508059
Related Subjects
N30130* -Metals
Ceramics
& Other Materials-Metals & Alloys-Properties Evaluations
ANNEALING
AUSTENITE
COLD WORKING
FAILURES
HIGH TEMPERATURE
MECHANICAL PROPERTIES
RUPTURE
SODIUM
STAINLESS STEEL-304
STAINLESS STEEL-316
STAINLESS STEELS
STRESSES
TIME
STAINLESS STEEL/stress-rupture properties of cold- worked and annealed Types 304 and 316
in sodium at 1000 to 1400$sup 0$F
biaxial
SODIUM/effects on biaxial stress-rupture properties of austenitic stainless steels at 1000 to 1400-F
Ceramics
& Other Materials-Metals & Alloys-Properties Evaluations
ANNEALING
AUSTENITE
COLD WORKING
FAILURES
HIGH TEMPERATURE
MECHANICAL PROPERTIES
RUPTURE
SODIUM
STAINLESS STEEL-304
STAINLESS STEEL-316
STAINLESS STEELS
STRESSES
TIME
STAINLESS STEEL/stress-rupture properties of cold- worked and annealed Types 304 and 316
in sodium at 1000 to 1400$sup 0$F
biaxial
SODIUM/effects on biaxial stress-rupture properties of austenitic stainless steels at 1000 to 1400-F