Microstructure and nanoscale composition analysis of the mechanical alloying of Fe{sub X}Cu{sub 100{minus}X} (X = 16, 60)
- Chinese Academy of Sciences, Shenyang (China). Lab. of Atomic Imaging of Solids
The microstructures of Fe{sub 16}Cu{sub 84} and Fe{sub 60}Cu{sub 40} (atomic percent) during mechanical alloying (MA) were studied by high resolution electron microscopy (HREM). Nanoscale composition distribution in Fe{sub 16}Cu{sub 84} was determined using a HF 2000 FEG TEM. In the Fe{sub 16}Cu{sub 84} specimen, a number of deformation twins were observed. In the Fe{sub 60}Cu{sub 40} specimen, shear band and generation of nanocrystals in the shear band were observed, which is shown to be a typical mechanism for grain size reduction during MA. In both specimens, the b.c.c. grains tend to be very small (<5 nm) before alloying, which is shown to be a prerequisite condition for the dissolution of Fe in Cu and is also direct evidence to support the thermodynamical model proposed by Yavari et al. Nanoscale composition analysis in Fe{sub 16}Cu{sub 84} specimen shows that the average Fe contents in both the interior of grains and the grain boundaries (GBs) are close to the designed composition, thus proving that a supersaturated solid solution has really formed. However, the Fe contents in both cases are rather inhomogeneous, indicating that the mixing of Fe and Cu during MA is inhomogeneous. The process of MA is suggested to be divided into two stages: at the early stage, the grain sizes reduce quickly to a steady value due to the mobility of dislocations; further deformation can be fully accommodated by GBs. As a result, very fast volume diffusion and GB diffusion are achieved. NC-structure and greatly enhanced diffusion coefficients allow the formation of supersaturated solid solutions in immiscible systems with positive enthalpy of mixing.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 445328
- Journal Information:
- Acta Materialia, Vol. 45, Issue 1; Other Information: PBD: Jan 1997
- Country of Publication:
- United States
- Language:
- English
Similar Records
Misorientation dependence of nanometer grain boundary sliding of [011] twist boundaries in copper
An internal stress induced by node-blocked grain boundary sliding and associated backward sliding