Nickel aluminide-copper backing for butt joint welding
Book
·
OSTI ID:442955
- Auburn Univ., AL (United States)
- Hobart Brothers Inc., Troy, OH (United States)
Single-side full penetration welding is the primary welding process in shipbuilding. This process requires the use of a backing to support the molten metal. Conventionally, copper has been used as the backing material in the shop and ceramic tiles for jobs on the field. However, copper has shown to contaminate the weld and produce adverse effects and ceramics have shown to produce porosities in the weld. A new backing with an intermetallic layer (NiAl) on the copper surface has been fabricated. The results indicate that this backing could alleviate the contamination problems and produce quality welds.
- OSTI ID:
- 442955
- Report Number(s):
- CONF-950682-; ISBN 0-87170-567-2; TRN: IM9712%%380
- Resource Relation:
- Conference: 4. international conference on trends in welding research, Gatlinburg, TN (United States), 5-9 Jun 1995; Other Information: PBD: 1996; Related Information: Is Part Of Trends in welding research: Proceedings of the 4. international conference; Smartt, H.B.; Johnson, J.A. [eds.] [Idaho National Engineering Lab., Idaho Falls, ID (United States)]; David, S.A. [ed.] [Oak Ridge National Lab., TN (United States)]; PB: 836 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Development of ceramic-coated weld backing bars
FABRICATION OF THE MOLTEN-SALT REACTOR EXPERIMENT HEAT EXCHANGER CORE INVOLVES A NOVEL WELDED AND BACK-BRAZED JOINT DESIGN FOR TUBE-TO-TUBE SHEET JOINTS
Microstructure evolution of Al/Mg butt joints welded by gas tungsten arc with Zn filler metal
Technical Report
·
Thu Oct 20 00:00:00 EDT 1994
·
OSTI ID:442955
FABRICATION OF THE MOLTEN-SALT REACTOR EXPERIMENT HEAT EXCHANGER CORE INVOLVES A NOVEL WELDED AND BACK-BRAZED JOINT DESIGN FOR TUBE-TO-TUBE SHEET JOINTS
Journal Article
·
Sat Feb 01 00:00:00 EST 1964
· Welding J. (N.Y.)
·
OSTI ID:442955
Microstructure evolution of Al/Mg butt joints welded by gas tungsten arc with Zn filler metal
Journal Article
·
Sun Jul 15 00:00:00 EDT 2012
· Materials Characterization
·
OSTI ID:442955