Ceramic bearing development. Volume 3. Development of a thermal proof test for silicon nitride balls. Interim report, 1 August 1992-1 October 1994
Technical Report
·
OSTI ID:442287
The Major objective of the Development of a Thermal Proof Test for Silicon Nitride Balls was to improve hybrid bearing reliability by the elimination of critical size flaws that cause early failures. The two main tasks in this effort were the demonstration of a thermal proof test method, and the fatigue life testing of thermal proof tested balls. A thermal proof test based on fracture mechanics was developed. A Weibull Relationship was observed between thermal quench temperature deltaT, and the probability of crack extension. Three hundred 7/16 in. NBD-200 balls were thermal proof tested and optically inspected. 224 of these, judged `acceptable`, were tested in hybrid bearings, at 2.9 Mpa (420 KSI) contract stress. Post-mortem analysis of failures in the hybrid bearing tests indicated that proof testing may have promoted failures in balls that, although flawed, may have otherwise performed satisfactorily. Thermal proof testing may be more useful as a sample inspection for lot qualification and process improvement studies, rather than for inspection of balls to be used in critical applications.
- Research Organization:
- Cerbec, Inc., East Granby, CT (United States)
- OSTI ID:
- 442287
- Report Number(s):
- AD-A--317564/3/XAB; CNN: Contract F33615-92-C-5917
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ceramic bearing development, Volume 2. Development of surface acoustic wave NDE for silicon nitride balls. Interim report, 1 July 1992-1 October 1994
Ceramic bearing development. Volume 1. Fatigue and wear behavior of NBD-200 silicon nitride balls. Interim report, 1 August 1992-1 October 1994
Ceramic bearing development. Silicon nitride bearing balls of improved reliability: Thermal oxidation. Final report, 1 January 1995-31 October 1996
Technical Report
·
Tue Feb 28 23:00:00 EST 1995
·
OSTI ID:442285
Ceramic bearing development. Volume 1. Fatigue and wear behavior of NBD-200 silicon nitride balls. Interim report, 1 August 1992-1 October 1994
Technical Report
·
Tue Feb 28 23:00:00 EST 1995
·
OSTI ID:445722
Ceramic bearing development. Silicon nitride bearing balls of improved reliability: Thermal oxidation. Final report, 1 January 1995-31 October 1996
Technical Report
·
Thu Oct 31 23:00:00 EST 1996
·
OSTI ID:512652