Effect of plastic deformation on electrical resistivity of molybdenum monocrystals (in Russian)
Journal Article
·
· Probl. Proch. Mashinostr., no. 2, pp. 73-75
OSTI ID:4418350
The effect of crystal lattice defects, due to plastic deformation of monocrystal molybdenum, on changes in electrical resistance at 4.2 deg K was studied. For separation of the contribution of vacancies and dislocations to electrical resistance, samples were annealed at 800 deg K after deformation. It was established that the residual resistance due to vacancies in molybdenum was 4 x 10/sup -5/ ohm cm/at.% and that due to dislocations of the order of 10/sup -16/ ohm cm/sup 3/. (tr-auth)
- Research Organization:
- Inst. of Metallurgy, Moscow
- NSA Number:
- NSA-29-000976
- OSTI ID:
- 4418350
- Journal Information:
- Probl. Proch. Mashinostr., no. 2, pp. 73-75, Journal Name: Probl. Proch. Mashinostr., no. 2, pp. 73-75; ISSN PPMMA
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
PLASTIC PROPERTIES OF BERYLLIUM MONOCRYSTALS. II
PLASTIC DEFORMATION AND RUPTURE OF URANIUM MONOCRYSTALS BY TRACTION AT-196 C
EFFECTS OF TEMPERATURE AND RATE AND DEGREE OF DEFORMATION ON CARBON STEEL RESISTANCE TO PLASTIC DEFORMATION
Journal Article
·
Wed Dec 31 23:00:00 EST 1958
· Fiz. Metal. i Metalloved
·
OSTI ID:4205948
PLASTIC DEFORMATION AND RUPTURE OF URANIUM MONOCRYSTALS BY TRACTION AT-196 C
Journal Article
·
Mon Jul 30 00:00:00 EDT 1962
· Compt. Rend.
·
OSTI ID:4734160
EFFECTS OF TEMPERATURE AND RATE AND DEGREE OF DEFORMATION ON CARBON STEEL RESISTANCE TO PLASTIC DEFORMATION
Journal Article
·
Sat Nov 30 23:00:00 EST 1957
· Izvest. Akad. Nauk S.S.S.R. Otdel. Tekh. Nauk
·
OSTI ID:4347185