Studies on ferric oxide hydroxides. 3: Adsorption of selenite (SeO{sub 3}{sup 2{minus}}) on different forms of iron oxyhydroxides
Journal Article
·
· Journal of Colloid and Interface Science
- Regional Research Lab., Orissa (India)
Adsorption of selenite (SeO{sub 3}{sup 2{minus}}) on different polymorphic forms of iron oxyhydroxides and amorphous ferrihydrite was studied as a function of time, temperature, pH, and concentration of adsorbate(s) and adsorbent(s). Analysis of adsorption data indicates that the surfaces of all the forms of oxyhydroxides and ferrihydrite are heterogeneous in nature and that adsorption fits into a heterogeneous site binding model. The adsorption capacity of oxyhydroxides for SeO{sub 3}{sup 2{minus}} follows the order {beta}-FeOOH < {alpha}-FeOOH < {gamma}-FeOOH < {delta}-FeOOH < ferrihydrite.
- OSTI ID:
- 438892
- Journal Information:
- Journal of Colloid and Interface Science, Journal Name: Journal of Colloid and Interface Science Journal Issue: 2 Vol. 185; ISSN 0021-9797; ISSN JCISA5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Studies on Indian Ocean manganese nodules. 3: Adsorption of aqueous selenite on ferromanganese nodules
XPS studies on the electronic structure of bonding between solid and solutes: Adsorption of arsenate, chromate, phosphate, Pb{sup 2+}, and Zn{sup 2+} ions on amorphous black ferric oxyhydroxide
Kinetics of selenate and selenite adsorption/desorption at the goethite/water interface
Journal Article
·
Fri Mar 14 23:00:00 EST 1997
· Journal of Colloid and Interface Science
·
OSTI ID:483810
XPS studies on the electronic structure of bonding between solid and solutes: Adsorption of arsenate, chromate, phosphate, Pb{sup 2+}, and Zn{sup 2+} ions on amorphous black ferric oxyhydroxide
Journal Article
·
Fri Mar 31 23:00:00 EST 2000
· Geochimica et Cosmochimica Acta
·
OSTI ID:20020885
Kinetics of selenate and selenite adsorption/desorption at the goethite/water interface
Journal Article
·
Fri Nov 30 23:00:00 EST 1990
· Environmental Science and Technology; (USA)
·
OSTI ID:5928736