STRENGTH OF JOINTS IN ALUMINUM ALLOYS 61S-T6 AND 52S-H34 WELDED BY THE SEMIAUTOMATIC INERT-GAS METAL-ARC PROCESS USING 43S ALUMINUM ALLOY FILLER METAL
Technical Report
·
OSTI ID:4383958
- Research Organization:
- Industrial Test Lab., Philadelphia Naval Shipyard
- NSA Number:
- NSA-09-003508
- OSTI ID:
- 4383958
- Report Number(s):
- ITL-4135; U-63691
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-55
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
DETERMINATION OF THE CAUSES OF WELD-METAL CRACKING IN HIGH-STRENGTH STEELS AND THE DEVELOPMENT OF HEAT-TREATABLE LOW-ALLOY-STEEL FILLER WIRES FOR USE WITH THE INERT-GAS-SHIELDED ARC-WELDING PROCESS. Period covered: June 16, 1958 to July 30, 1959
THE IMPROVEMENT IN WELD SOUNDNESS BY THE USE OF HALOGENS AND HALIDES IN INERT GAS METAL ARC WELDING OF ALUMINUM. Phase Report No. 1 for August 1, 1954 to July 31, 1955 on THE WELDING OF HIGH STRENGTH ALUMINUM ALLOYS
Welding procedure specification. Supplement 1. Records of procedure qualification tests. Manual gas tungsten arc (DC) and semiautomatic gas metal arc welding of 6XXX aluminum. [6061 and 6063]
Technical Report
·
Tue Nov 10 00:00:00 EST 1959
·
OSTI ID:4383958
THE IMPROVEMENT IN WELD SOUNDNESS BY THE USE OF HALOGENS AND HALIDES IN INERT GAS METAL ARC WELDING OF ALUMINUM. Phase Report No. 1 for August 1, 1954 to July 31, 1955 on THE WELDING OF HIGH STRENGTH ALUMINUM ALLOYS
Technical Report
·
Fri Dec 30 00:00:00 EST 1955
·
OSTI ID:4383958
Welding procedure specification. Supplement 1. Records of procedure qualification tests. Manual gas tungsten arc (DC) and semiautomatic gas metal arc welding of 6XXX aluminum. [6061 and 6063]
Technical Report
·
Sun Jun 01 00:00:00 EDT 1986
·
OSTI ID:4383958