STUDIES ON THE ANODIC POLARIZATION OF ZIRCONIUM. I. THE FORMATION FIELD FROM BOTH HIGH-POTENTIAL AND LOW-POTENTIAL MEASUREMENTS. II. POROSITY OF VERY THIN ANODIC OXIDE FILMS. III. THICKNESSES OF VERY THIN AIR-FORMED OXIDE FILMS. IV. A LOW-POTENTIAL CURRENT-VOLTAGE REGULATOR
Technical Report
·
OSTI ID:4367172
- Research Organization:
- Oregon. Univ., Eugene
- DOE Contract Number:
- AT(45-1)-535
- NSA Number:
- NSA-10-000561
- OSTI ID:
- 4367172
- Report Number(s):
- AECU-3058
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-56
- Country of Publication:
- United States
- Language:
- English
Similar Records
STUDIES ON THE ANODIC POLARIZATION OF ZIRCONIUM--GROWTH RATES AND THICKNESSES OF THE VERY THIN ANODIC OXIDE FILMS
FORMATION FIELDS AND CURRENT EFFICIENCIES IN THE ANODIC OXIDATION OF ZIRCONIUM: A DIRECT COMPARISON OF HIGH-POTENTIAL FORMATION FIELDS WITH THOSE DERIVED FROM LOW-POTENTIAL CHARGING CURVES
TEMPERATURE DEPENDENCE OF TAFEL SLOPE IN THE FORMATION OF VERY THIN ANODIC OXIDE FILMS ON NIOBIUM
Technical Report
·
Thu Jul 01 00:00:00 EDT 1954
·
OSTI ID:4367172
FORMATION FIELDS AND CURRENT EFFICIENCIES IN THE ANODIC OXIDATION OF ZIRCONIUM: A DIRECT COMPARISON OF HIGH-POTENTIAL FORMATION FIELDS WITH THOSE DERIVED FROM LOW-POTENTIAL CHARGING CURVES
Technical Report
·
Tue Jan 01 00:00:00 EST 1957
·
OSTI ID:4367172
TEMPERATURE DEPENDENCE OF TAFEL SLOPE IN THE FORMATION OF VERY THIN ANODIC OXIDE FILMS ON NIOBIUM
Technical Report
·
Tue Jan 01 00:00:00 EST 1957
·
OSTI ID:4367172
Related Subjects
CHEMISTRY
AIR- ANODES- CHEMICAL REACTIONS- CONTROL SYSTEMS- CURRENTS- ELECTRIC POTENTIAL- ELECTRONIC EQUIPMENT- ELECTRONICS- FABRICATION- FILMS- LOW TEMPERATURE- MEASURED VALUES- NITRATES- OXIDATION- OXIDES- PLANNING- POLARIZATION- POROSITY- PRODUCTION- SOLUTIONS- SULFATES- THICKNESS- ZIRCONIUM- ZIRCONIUM OXIDES
AIR- ANODES- CHEMICAL REACTIONS- CONTROL SYSTEMS- CURRENTS- ELECTRIC POTENTIAL- ELECTRONICS- FILMS- LOW TEMPERATURE- MEASURED VALUES- NITRATES- OXIDATION- OXIDES- PLANNING- POLARIZATION- POROSITY- PRODUCTION- SOLUTIONS- SULFATES- THICKNESS- WEAR- ZIRCONIUM- ZIRCONIUM OXIDES
AIR- ANODES- CHEMICAL REACTIONS- CONTROL SYSTEMS- CURRENTS- ELECTRIC POTENTIAL- ELECTRONIC EQUIPMENT- ELECTRONICS- FABRICATION- FILMS- LOW TEMPERATURE- MEASURED VALUES- NITRATES- OXIDATION- OXIDES- PLANNING- POLARIZATION- POROSITY- PRODUCTION- SOLUTIONS- SULFATES- THICKNESS- ZIRCONIUM- ZIRCONIUM OXIDES
AIR- ANODES- CHEMICAL REACTIONS- CONTROL SYSTEMS- CURRENTS- ELECTRIC POTENTIAL- ELECTRONICS- FILMS- LOW TEMPERATURE- MEASURED VALUES- NITRATES- OXIDATION- OXIDES- PLANNING- POLARIZATION- POROSITY- PRODUCTION- SOLUTIONS- SULFATES- THICKNESS- WEAR- ZIRCONIUM- ZIRCONIUM OXIDES