SOME OBSERVATIONS ON URANIUM-RICH URANIUM RUTHENIUM ALLOYS
Technical Report
·
OSTI ID:4335072
The solidus and liquidus depressions in U-rich U--Ru alloys are approximately 5 and 1 deg C for 0.1 at.% Ru addition, respectively. A eutectic occurs at 900 deg C and 18 at.% Ru between U and an intermetallic compound of unknown compesition. The alpha yields beta and beta yields gamma transformation temperatures in U are lowered by additions of Ru, but in alloys containing up to 20 at.% Ru sharp arrests can be detected at heating and cooling rates of 11/2 deg C/min. The solubility of Ru in gamma uranium is approximately 10 at.% at 900 deg C, the solability in alpha uranium being considerably lower. (auth)
- Research Organization:
- Gt. Brit. Atomic Energy Research Establishment, Harwell, Berks, England
- NSA Number:
- NSA-12-000271
- OSTI ID:
- 4335072
- Report Number(s):
- AERE-M/M-107(Del.)
- Country of Publication:
- United Kingdom
- Language:
- English
Similar Records
THE URANIUM-IRON SYSTEM
THE URANIUM-RHENIUM ALLOY SYSTEM
THE URANIUM-RHENIUM ALLOY SYSTEM
Technical Report
·
Tue May 31 00:00:00 EDT 1949
·
OSTI ID:4789747
THE URANIUM-RHENIUM ALLOY SYSTEM
Journal Article
·
Sat Nov 30 23:00:00 EST 1963
· J. Less-Common Metals
·
OSTI ID:4093338
THE URANIUM-RHENIUM ALLOY SYSTEM
Technical Report
·
Sun Jan 13 23:00:00 EST 1963
·
OSTI ID:4647063