CORROSION OF AN ALUMINUM-NICKEL ALLOY IN A REACTOR TEST LOOP
The results of the corrosion study are illustrated in a plot of the weight loss of the aluminum--nickel samples with respect to the time at test temperatures of 470 to 485 deg F. The corrosion rate determined by this test indicates that the weight loss per unit time is the same for both the in-pile irradiated specimens and the out-of-pile control specimens which did not have any neutron exposure, except that the out-of-pile specimens had a higher initial rate of corrosion which elevated the curve above that of the in-pile specimens. (auth)
- Research Organization:
- Argonne National Lab., Lemont, Ill.
- DOE Contract Number:
- W-31109-ENG-38
- NSA Number:
- NSA-12-000227
- OSTI ID:
- 4332526
- Report Number(s):
- ANL-5783
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE CORROSION OF ALUMINUM ALLOYS IN HIGH-VELOCITY WATER AT 170 TO 290 C
URANIUM-BISMUTH IN-PILE CORROSION TEST LOOP. RADIATION LOOP NO. 1
CORROSION BEHAVIOUR OF ALUMINUM-NICKEL-IRON ALLOYS IN HIGH TEMPERATURE WATER UNDER DYNAMIC CONDITIONS
Technical Report
·
Thu Jun 15 00:00:00 EDT 1961
·
OSTI ID:4001856
URANIUM-BISMUTH IN-PILE CORROSION TEST LOOP. RADIATION LOOP NO. 1
Technical Report
·
Mon May 01 00:00:00 EDT 1961
·
OSTI ID:4749855
CORROSION BEHAVIOUR OF ALUMINUM-NICKEL-IRON ALLOYS IN HIGH TEMPERATURE WATER UNDER DYNAMIC CONDITIONS
Technical Report
·
Sun Nov 30 23:00:00 EST 1958
·
OSTI ID:4146183