FOLD FORMATION AND GRAIN BOUNDARY SLIDING DURING CREEP
Technical Report
·
OSTI ID:4321960
The accommodation process of fold formation which occurs in the grains when grain boundary sliding takes place has been studied. Specimens of Al, Al-- 20% Zn, and Al--Cu alloys were deformed in creep. The process of deformation was observed either directly during creep or after the specimen had been unloaded. Aluminum--20% Zn specimens were also quenched and aged, and the preferential precipitation occurring on aging was studied in relation to fold formation. (auth)
- Research Organization:
- Massachusetts Inst. of Tech., Cambridge
- DOE Contract Number:
- AT(30-1)-1973
- NSA Number:
- NSA-12-004192
- OSTI ID:
- 4321960
- Report Number(s):
- NYO-4771
- Resource Relation:
- Other Information: Orig. Receipt Date: 31-DEC-58
- Country of Publication:
- United States
- Language:
- English
Similar Records
MEASUREMENTS OF DEFORMATION RESULTING FROM GRAIN BOUNDARY SLIDING IN ALUMINUM AND ALUMINUM-MAGNESIUM ALLOYS FROM 410 TO 940 F
Investigation of grain boundary sliding and cavitation during creep of single-phase alumina. Ph.D. Thesis
Grain-boundary sliding and deformation mechanisms during high-temperature creep. Final report
Technical Report
·
Sat Feb 01 00:00:00 EST 1958
·
OSTI ID:4321960
Investigation of grain boundary sliding and cavitation during creep of single-phase alumina. Ph.D. Thesis
Thesis/Dissertation
·
Sat Jan 01 00:00:00 EST 1994
·
OSTI ID:4321960
Grain-boundary sliding and deformation mechanisms during high-temperature creep. Final report
Technical Report
·
Sun Feb 01 00:00:00 EST 1981
·
OSTI ID:4321960