EFFECT OF NEUTRON IRRADIATION ON THE ROOM TEMPERATURE TENSILE PROPERTIES OF ZIRCALOY-3
Technical Report
·
OSTI ID:4299498
S>Zircaloy-3 tensile specimens removed from 25% cold-rolled and annealed plate in both the longitudinal and transverse directions were irradiated at the MTR at temperatures of 115 F and to integrated fast neutron fluxes ranging from 1,2 x 10/sup 20/ nvt to 3.4 x 10/sup 20/ nvt. There were indications that saturation of radiation damage may have been reached, although more experimental work is needed to verify this effect. The uniform elongations were reduced by 77 and 100% in the longitudinal and transverse directions, respectively. (auth)
- Research Organization:
- Knolls Atomic Power Lab., Schenectady, N.Y.
- DOE Contract Number:
- W-31-109-ENG-52
- NSA Number:
- NSA-13-000422
- OSTI ID:
- 4299498
- Report Number(s):
- KAPL-M-RLM-17
- Country of Publication:
- United States
- Language:
- English
Similar Records
EFFECTS OF COLD WORK AND NEUTRON IRRADIATION ON THE TENSILE PROPERTIES OF ZIRCALOY-2
THE EFFECTS OF COLD WORK AND NEUTRON IRRADIATION ON THE TENSILE PROPERTIES OF ZIRCALOY-2
THE EFFECTS OF LOW NEUTRON EXPOSURES AT LOW TEMPERATURES ON THE HARDNESS AND TENSILE PROPERTIES OF NATURAL URANIUM
Technical Report
·
Sun Mar 31 23:00:00 EST 1963
·
OSTI ID:4690313
THE EFFECTS OF COLD WORK AND NEUTRON IRRADIATION ON THE TENSILE PROPERTIES OF ZIRCALOY-2
Technical Report
·
Wed Apr 17 23:00:00 EST 1963
·
OSTI ID:4693974
THE EFFECTS OF LOW NEUTRON EXPOSURES AT LOW TEMPERATURES ON THE HARDNESS AND TENSILE PROPERTIES OF NATURAL URANIUM
Technical Report
·
Mon Jun 01 00:00:00 EDT 1959
·
OSTI ID:4221866