HARDENING OF COPPER SINGLE CRYSTALS IRRADIATED AT-195 C
Single crystals of Cu were electropolished, sealed in silica quills, and irradiated in the Harwell reactor BEPO for one week at -195 deg C. The total dose of slow neutrons was 8 x 10/sup 17/ n/cm/sup 2/, and the ratio of fast to thermal flux was about unity in the position used. After irradiaiion the specimens were stored in liquid nitrogen to allow the radioactivity to decrease and were then transferred to the tensile machine and tested at - 195 deg C without permitting the temperature to rise. The stressstrain curves for the irradiated specimens are presented. (W.L.H.)
- Research Organization:
- Atomic Energy Research Establishment, Harwell, Berks, Eng.
- NSA Number:
- NSA-13-008210
- OSTI ID:
- 4271499
- Journal Information:
- Acta Met., Journal Name: Acta Met. Vol. Vol: 6
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
THE HARDENING OF COPPER SINGLE CRYSTALS BY ELECTRON IRRADIATION
UNLOADING EFFECTS IN THE PLASTIC PROPERTIES OF COPPER SINGLE CRYSTALS
Evidence for the trapping of interstitial atoms in irradiated tungsten
Journal Article
·
Wed Feb 28 23:00:00 EST 1962
· Acta Met.
·
OSTI ID:4796482
UNLOADING EFFECTS IN THE PLASTIC PROPERTIES OF COPPER SINGLE CRYSTALS
Journal Article
·
Fri Feb 28 23:00:00 EST 1958
· Phil. Mag.
·
OSTI ID:4344792
Evidence for the trapping of interstitial atoms in irradiated tungsten
Journal Article
·
Mon Mar 31 23:00:00 EST 1958
· Philosophical Magazine
·
OSTI ID:4348656