INVESTIGATIONS OF NiO-ZnO-Fe$sub 2$$O$$sub 3$ SYSTEMS (in Russian)
Journal Article
·
· Izvest. Akad. Nauk S.S.S.R., Ser. Fiz.
OSTI ID:4245630
The phase composition of NiO- ZnO-F/sub 2/O/sub 3/ systems and their solubilities in stoichiometric Ni- Zn ferrites were determined on the basis of x- ray analysis and the regularities in Curie point variations. Ring-shaped spccimens of NiO- ZnO- Fe/sub 2/O/sub 3/ were sintered at temperatures of 1110, 1240, 1320, 1375, and 1420 deg C, and cooled down to 1100 deg C at 100 deg per hour, 1100 to 900 deg C at 80 deg per hour, 900 to 500 deg C at 40 deg per hour, and 500 to 200 deg C at 20 deg per hour. At 200 deg the specimens were taken out of the furnace. Constitution diagrams of the tests are included. (R.V.J.)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-13-015388
- OSTI ID:
- 4245630
- Journal Information:
- Izvest. Akad. Nauk S.S.S.R., Ser. Fiz., Vol. Vol: 23; Other Information: Orig. Receipt Date: 31-DEC-59
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
Preparation and photocatalytic activity of ZnO/TiO{sub 2}/SnO{sub 2} mixture
Dynamic and static photoresponse of ultraviolet-detecting thin-film transistors based on transparent NiO{sub x} electrodes and an n-ZnO channel
Coprecipitation of nickel zinc malonate: A facile and reproducible synthesis route for Ni{sub 1−x}Zn{sub x}O nanoparticles and Ni{sub 1−x}Zn{sub x}O/ZnO nanocomposites via pyrolysis
Journal Article
·
Tue Nov 15 00:00:00 EST 2005
· Journal of Solid State Chemistry
·
OSTI ID:4245630
+1 more
Dynamic and static photoresponse of ultraviolet-detecting thin-film transistors based on transparent NiO{sub x} electrodes and an n-ZnO channel
Journal Article
·
Fri Apr 01 00:00:00 EST 2005
· Journal of Applied Physics
·
OSTI ID:4245630
+1 more
Coprecipitation of nickel zinc malonate: A facile and reproducible synthesis route for Ni{sub 1−x}Zn{sub x}O nanoparticles and Ni{sub 1−x}Zn{sub x}O/ZnO nanocomposites via pyrolysis
Journal Article
·
Thu Oct 15 00:00:00 EDT 2015
· Journal of Solid State Chemistry
·
OSTI ID:4245630
+2 more