TENSILE TESTS ON ZIRCONIUM SAMPLES (in French)
Journal Article
·
· Mem. sci. rev. met.
OSTI ID:4221374
Tensile tests were made on zirconium cold rolled or rolled at 400 deg C. After rolling the samples were annealed in vacuo between 400 and 800 deg C. The tensile strength and the hardness vary in the same manner and, for small degrees of reduction, increase after annealing at about 500 deg C. The cold-rolled metal has a lower percentage elongation than all other samples. The tensile curve ior metal heavilyrolled at 400 deg C and annealed at 500 deg C shows a plateau at the plastic limit. (tr-auth)
- Research Organization:
- Originating Research Org. not identified
- NSA Number:
- NSA-14-003821
- OSTI ID:
- 4221374
- Journal Information:
- Mem. sci. rev. met., Journal Name: Mem. sci. rev. met. Vol. Vol: 56
- Country of Publication:
- Country unknown/Code not available
- Language:
- French
Similar Records
THE EFFECTS OF HEAT TREATMENTS ON THE HARDNESS AND TENSILE PROPERTIES OF COLD ROLLED IODIDE HAFNIUM
Influence of Rolling and Annealing Conditions on Texture and Mechanical Properties of Zirconium; INFLUENCE DES CONDITIONS DE LAMINAGE ET DE RECUIT SUR LA TEXTURE ET LES PROPRIETES MECANIQUES DU ZIRCONIUM
A STUDY OF IRRADIATION EFFECTS IN TYPE "A" NICKEL AND TYPE 347 STAINLESS STEEL TENSILE SPECIMENS. Final Report of Program 6.10.2
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4804156
Influence of Rolling and Annealing Conditions on Texture and Mechanical Properties of Zirconium; INFLUENCE DES CONDITIONS DE LAMINAGE ET DE RECUIT SUR LA TEXTURE ET LES PROPRIETES MECANIQUES DU ZIRCONIUM
Thesis/Dissertation
·
Fri Jun 27 00:00:00 EDT 1958
·
OSTI ID:4086106
A STUDY OF IRRADIATION EFFECTS IN TYPE "A" NICKEL AND TYPE 347 STAINLESS STEEL TENSILE SPECIMENS. Final Report of Program 6.10.2
Technical Report
·
Fri Jul 01 00:00:00 EDT 1960
·
OSTI ID:4138827