OBSERVATIONS ON THE SYSTEM ZIRCONIUM IRON
Journal Article
·
· Trans. Met. Soc. AI,E
OSTI ID:4198987
The solubility of iron in zirconium was determined to be between 0.017 and 0.025 wt.% in the alpha -phase. The observation of fine ZrFe/sub 2/ particles in a specimen of 0.012 wt.% Fe alloy quenched from 700 deg C indicates that the solubility drops below this composition at 700 deg C and lower. A singlephase ZrFe/sub 2/ x-ray diffraction pattern from an alloy of 54.81 wt.% Fe was observed with a melting point of 1650 deg melting points for 47.42 and 49.52 wt.% Fe alloys were determined to be 1590 and 1640 deg C respectively. (C.J.G.)
- Research Organization:
- Republic Aviation Corp., Farmingdale, N.Y.; Armour Research Foundation, Chicago
- NSA Number:
- NSA-14-005626
- OSTI ID:
- 4198987
- Journal Information:
- Trans. Met. Soc. AI,E, Journal Name: Trans. Met. Soc. AI,E Vol. Vol: 215
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
THE SYSTEM ZIRCONIUM-IRON-TIN. Summary Report No. 5 for July 1, 1957-- June 30, 1958
STUDIES OF ZIRCONIUM-IRON-TIN ALLOYS. Report No. 6 (Final) for July 1, 1958-March 31, 1959
CONSTITUTION DIAGRAM OF ZrCr$sub 2$-ZrFe$sub 2$ ALLOYS
Technical Report
·
Tue Jul 29 00:00:00 EDT 1958
·
OSTI ID:4303115
STUDIES OF ZIRCONIUM-IRON-TIN ALLOYS. Report No. 6 (Final) for July 1, 1958-March 31, 1959
Technical Report
·
Thu Apr 30 00:00:00 EDT 1959
·
OSTI ID:4265568
CONSTITUTION DIAGRAM OF ZrCr$sub 2$-ZrFe$sub 2$ ALLOYS
Journal Article
·
Sun Dec 31 23:00:00 EST 1961
· Sbornik Nauchnykh Trudov Instituta Metallofiziki, Akademiya Nauk Ukrainskoi SSR (Ukrainian S.S.R.)S.R.)
·
OSTI ID:4747189