- Sandia National Labs., Albuquerque, NM (United States). Physical and Joining Metallurgy Dept.
Experiments designed to assess the fabrication and service weldability of 304B4A borated stainless steel were conducted. Welding procedures and parameters for manual gas tungsten arc (GTA) welding, autogenous electron beam (EB) welding and filler-added EB welding were developed and found to be similar to those for austenitic stainless steels. Following the procedure development, four test welds were produced and evaluated by microstructural analysis and Charpy impact testing. Further samples were used for determination of the postweld heat treatment (PWHT) response of the welds. The fusion zone structure of welds in this alloy consists of primary austenite dendrites with an interdendritic eutectic-like austenite/boride constituent. Welds also show an appreciable partially molten zone that consists of the austenite/boride eutectic surrounding unmelted austenite islands. The microstructure of the EB welds was substantially finer than that of the GTA welds, and boride coarsening was not observed in the solid state heat-affected zone (HAZ) of either weld type. The impact toughness of as-welded samples was found to be relatively poor, averaging less than 10 J for both GTA and EB welds. For fusion zone notched GTA and EB samples and centerline notched EB samples, fracture generally occurred along the boundary between the partially molten and solid-state regions of the HAZ. The results of the PWHT study were very encouraging, with typical values of the impact energy for HAZ notched samples approaching 40 J, or twice the minimum code-acceptable value.
- Research Organization:
- Sandia National Laboratory
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 419751
- Journal Information:
- Welding Journal, Journal Name: Welding Journal Journal Issue: 1 Vol. 76; ISSN WEJUA3; ISSN 0043-2296
- Country of Publication:
- United States
- Language:
- English
Similar Records
The influence of weld thermal cycles on the microstructure and toughness of duplex stainless steels
Microstructure evolution in the fusion welding of heat-treatable Al-Cu-Li alloys. Ph.D. Thesis