CORROSION CRACKING OF LOW-CARBON STAINLESS STEEL (in Russian)
Journal Article
·
· Doklady Akad. Nauk S.S.S.R.
OSTI ID:4194096
Studies were made of corrosion, mechanical properties, and corrosion cracking of low-carbon stainless steel 1 X l8H9 (0.10%C). It was found thst variations of carbon concentration from 0.1 to 0.014% do not affect the resistance to corrosion cracking in 42% boiling solution of MgCl/sub 2/(R.V.J.)
- Research Organization:
- Baikov Inst. of Metallurgy, Academy of Sciences, USSR
- NSA Number:
- NSA-14-008692
- OSTI ID:
- 4194096
- Journal Information:
- Doklady Akad. Nauk S.S.S.R., Journal Name: Doklady Akad. Nauk S.S.S.R. Vol. Vol: 129
- Country of Publication:
- Country unknown/Code not available
- Language:
- Russian
Similar Records
EFFECTS OF CARBON ON X18H9 STAINLESS STEEL CORROSION CRACKING
EFFECT OF SOME INHIBITORS ON THE CORROSION CRACKING OF STEEL 1X18N9 IN 42% MgCl$sub 2$ SOLUTION
Stress-Corrosion Cracking of Type 347 Stainless Steel And Other Alloys in High Temperature Water
Journal Article
·
Sun Oct 01 00:00:00 EDT 1961
· Zhur. Priklad. Khim.
·
OSTI ID:4805002
EFFECT OF SOME INHIBITORS ON THE CORROSION CRACKING OF STEEL 1X18N9 IN 42% MgCl$sub 2$ SOLUTION
Journal Article
·
Fri Mar 31 23:00:00 EST 1961
· Zhur. Fiz. Khim.
·
OSTI ID:4064231
Stress-Corrosion Cracking of Type 347 Stainless Steel And Other Alloys in High Temperature Water
Journal Article
·
Tue Oct 01 00:00:00 EDT 1963
· Corrosion (Houston)
·
OSTI ID:4629902