SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Quarterly Report No. 1 for May 13 to August 31, 1959
Technical Report
·
OSTI ID:4190079
Uranium monocarbide powder having a UC content of about 97% was produced by heating a mixture of UO/sub 2/ and carbon in a vacuum furnace at 1800 deg C. Uranium monocarbide pellets having a density of about 10 grams per cubic centimeter were prepared. A few experiments indicated that nitrogen contamination in the atmosphere probably aids sintering of UC. Small quantities of U/sub 3/Si/sub 2/ were produced by quenching U - Si melts from about 1700 deg C. (W.L.H.)
- Research Organization:
- Carborundum Co. Research and Development Div., Niagara Falls, N.Y.
- NSA Number:
- NSA-14-001445
- OSTI ID:
- 4190079
- Report Number(s):
- ORO-212
- Country of Publication:
- United States
- Language:
- English
Similar Records
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Quarterly Report No. 2 Covering Period September 1 to November 30, 1959
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 5 for December 1 to December 31, 1959
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Summary Report, January 1, 1961-March 15, 1962
Technical Report
·
Sun Dec 13 23:00:00 EST 1959
·
OSTI ID:4189195
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Monthly Progress Report No. 5 for December 1 to December 31, 1959
Technical Report
·
Thu Dec 31 23:00:00 EST 1959
·
OSTI ID:4192790
SYNTHESIS AND FABRICATION OF REFRACTORY URANIUM COMPOUNDS. Summary Report, January 1, 1961-March 15, 1962
Technical Report
·
Tue May 01 00:00:00 EDT 1962
·
OSTI ID:4772940