PROPERTIES OF TITANIUM-VANADIUM-ZIRCONIUM ALLOYS
Technical Report
·
OSTI ID:4189522
Arc-melted Ti--V-- Zr alloys ranging in composition from 5 to 20 at.% V and 5 to 50 at.% Zr were investigated relative to hardness, hot workability, and room-temperature tensile propenties. Structural changes and aging response to test temperatures of 600 and 800 deg C were studied. A Ti--10V--10 Zr alloy solution treated at 600 deg C exhibited a yield strength of 75,800 psi. Aging the alloy for four hours at 450 deg C increased the yield strength to 142,900 psi. (C.J.G.)
- Research Organization:
- Bureau of Mines
- NSA Number:
- NSA-14-014050
- OSTI ID:
- 4189522
- Report Number(s):
- BM-RI-5604
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
THE HEAT TREATMENT, TRANSFORMATION REACTIONS, AND MECHANICAL PROPERTIES OF SOME HIGH-STRENGTH ZIRCONIUM-BASE ALLOYS
DEVELOPMENT OF NIOBIUM-BASE ALLOYS. Quarterly Progress Report No. 3 for November 1, 1958 to February 1, 1959
IMPROVED VANADIUM-BASE ALLOYS. Final Report for period December 1, 1960 to November 30, 1961
Technical Report
·
Wed Aug 01 00:00:00 EDT 1956
·
OSTI ID:4311559
DEVELOPMENT OF NIOBIUM-BASE ALLOYS. Quarterly Progress Report No. 3 for November 1, 1958 to February 1, 1959
Technical Report
·
Mon Feb 09 23:00:00 EST 1959
·
OSTI ID:4168105
IMPROVED VANADIUM-BASE ALLOYS. Final Report for period December 1, 1960 to November 30, 1961
Technical Report
·
Tue Dec 19 23:00:00 EST 1961
·
OSTI ID:4821407