LOW-TEMPERATURE EQUILIBRIA AMONG ZrO$sub 2$, ThO$sub 2$, AND UO$sub 2$
Journal Article
·
· Journal of the American Ceramic Society (U.S.)
Studies made on low-hafnium-content ZrO/sub 2/ show that the monoclinic- tetragonal inversion temperature is 1170 deg C, and it is raised to approximately 1190 deg C in the "natural" ZrO/sub 2/ which contains approximately 2% HfO/sub 2/. No explanation oould be found for the known marked hysteresis during cooling, when the reverse polymorphic transformation takes place at 1040 deg C. In the System ZrO/sub 2/-- ThO/sub 2/ the monoclinic-tetragonal ZrO/sub 2/ inve rsion temperature is lowered to 1000 deg C, although the maximum solid solution extent of ZrO/sub 2/ in ThO/sub 2/ and vice versa is approximately only 2% at this temperature. Relow about 400 deg C. under hydrothermal conditions it was possible to prepare a continuous, although metastable, series of solid solutions with the fluorite structure with compositions varying from ThO/sub 2/ to nearly pure ZrO/sub 2/. Contrary to earlier work only 8 mole% ZrO/sub 2/ dissolves in UO/sub 2/ and less than 4 mole% of UO/sub 2/ in ZrO/sub 2/ at temperatures up to 1300 deg C. A continuous series of solid solutions could be made between ThO/sub 2/ and UO/sub 2/ at 1300 deg C, and extensive defect fluorite solid solutions could be prepared between ThO/sub 2/ and U/sub 3/O/sub 8/; there is some evidence for exsolution into uranium-rich and thorium-rich members at low temperatures. (auth)
- Research Organization:
- Pennsylvania State Univ., University Park
- Sponsoring Organization:
- USDOE
- NSA Number:
- NSA-14-014085
- OSTI ID:
- 4189444
- Journal Information:
- Journal of the American Ceramic Society (U.S.), Journal Name: Journal of the American Ceramic Society (U.S.) Vol. Vol: 43; ISSN JACTA
- Country of Publication:
- Country unknown/Code not available
- Language:
- English
Similar Records
A METALLOGRAPHIC AND X-RAY STUDY OF THE UO$sub 2$-ZrO$sub 2$ SYSTEM
PHASE EQUILIBRIUM DIAGRAMS OF SYSTEMS UO$sub 2$-ZrO$sub 2$ AND ThO$sub 2$- ZrO$sub 2$
Magnetic susceptibilities of UO/sub 2/-ThO/sub 2/-ZrO/sub 2/ solid solutions
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4811936
PHASE EQUILIBRIUM DIAGRAMS OF SYSTEMS UO$sub 2$-ZrO$sub 2$ AND ThO$sub 2$- ZrO$sub 2$
Technical Report
·
Fri Oct 30 23:00:00 EST 1959
·
OSTI ID:4290613
Magnetic susceptibilities of UO/sub 2/-ThO/sub 2/-ZrO/sub 2/ solid solutions
Journal Article
·
Tue Jul 01 00:00:00 EDT 1986
· J. Solid State Chem.; (United States)
·
OSTI ID:5428309