INTERNAL-PRESSURE CREEP-RUPTURE TESTS OF ZIRCALOY-2 TUBING
Technical Report
·
OSTI ID:4171349
Stress-rupture tests were performed on unirradiated Zircaloy-1 at room temperature, 600, and 700 deg T. The results indicated that the ductility, defined as effective strain, is not significantly affected by time to rupture. At 600 deg F, the ductility was considerably greater than at room temperature or at 700 deg F. Depending on the conditions of test, the ductility values range from 16 to 77%.- (auth)
- Research Organization:
- Knolls Atomic Power Lab., Schenectady, N.Y.
- DOE Contract Number:
- W-31-109-ENG-52
- NSA Number:
- NSA-14-014058
- OSTI ID:
- 4171349
- Report Number(s):
- KAPL-2072
- Country of Publication:
- United States
- Language:
- English
Similar Records
STRAIN FATIGUE BEHAVIOR OF ZIRCALOY 2 AND 3 AT ROOM TEMPERATURE AND 550 F
Rupture and Internal Pressurization Creep of Nb-Modified Zircaloy-4 Tubing: Application to Dry Storage Feasibility
INTERMEDIATE TEMPERATURE CREEP AND RUPTURE BEHAVIOR OF TITANIUM AND TITANIUM BASE ALLOYS. PART III. EFFECTS OF HOT ROLLING, EMBRITTLEMENT, AND INTERSTITIAL ELEMENTS. Period covered: March 1, 1955 to December 31, 1955
Technical Report
·
Sun Nov 17 23:00:00 EST 1957
·
OSTI ID:4348257
Rupture and Internal Pressurization Creep of Nb-Modified Zircaloy-4 Tubing: Application to Dry Storage Feasibility
Conference
·
Mon Jul 01 00:00:00 EDT 2002
·
OSTI ID:21064635
INTERMEDIATE TEMPERATURE CREEP AND RUPTURE BEHAVIOR OF TITANIUM AND TITANIUM BASE ALLOYS. PART III. EFFECTS OF HOT ROLLING, EMBRITTLEMENT, AND INTERSTITIAL ELEMENTS. Period covered: March 1, 1955 to December 31, 1955
Technical Report
·
Sun Sep 01 00:00:00 EDT 1957
·
OSTI ID:4334168