REFRACTORY ALLOY FOIL ROLLING DEVELOPMENT PROGRAM. Interim Report No. 2, October 15, 1962-January 15, 1963
Technical Report
·
OSTI ID:4166290
The melting of three niobium-bsse alloy and two tandtalum-bsse alloy ingots by arc-casting is described. The alloys were Nb--10% W--1% Zr--0.1% C (D- 43), Nb-5% Mo--5% V--1% Zr (B-88), Nb--10% W--2 1/2% Zr (Nb-752), Ta--10% W, and Ta--8% W--2% Rf (T-111). The process consisted of hydrostatic compaction of elemental powders into electrodes followed by double consumable arc melting to yield 6-inch diameter ingots. Analytical and metallurgical testing of the ingots is described. (auth)
- Research Organization:
- Du Pont de Nemours(E.I.); Co. Metals Center, Baltimore
- NSA Number:
- NSA-18-000571
- OSTI ID:
- 4166290
- Report Number(s):
- AD-297246
- Country of Publication:
- United States
- Language:
- English
Similar Records
REFRACTORY ALLOY FOIL ROLLING DEVELOPMENT PROGRAM. Phase III Report, February 18, 1963-May 20, 1963
PILOT EVALUATION OF VANADIUM ALLOYS. Bimonthly Report No. 7, September 18, 1962-November 17, 1962
PROPERTIES OF ARC-MELTED CHROMIUM-BASE ALLOYS
Technical Report
·
Fri Oct 30 23:00:00 EST 1964
·
OSTI ID:4113656
PILOT EVALUATION OF VANADIUM ALLOYS. Bimonthly Report No. 7, September 18, 1962-November 17, 1962
Technical Report
·
Thu Dec 13 23:00:00 EST 1962
·
OSTI ID:4752261
PROPERTIES OF ARC-MELTED CHROMIUM-BASE ALLOYS
Technical Report
·
Mon Jul 14 00:00:00 EDT 1958
·
OSTI ID:4794114