PHASE CHANGE AND DISORDERING BY IRRADIATION OF THE COMPOUND U$sub 2$Mo (in French)
Journal Article
·
· J. Nuclear Materials
ABS>Plates of U/sub 2/Mo were homogenized at 1050 deg C and heated at 500 deg C for 7 days to obtain ordered, quadratic gamma ' phase. Irradiation by a thermal neutron flux at 2 x 10/sup 10/ to 2 x 10/sup 12/ n/cm/sup 2//sec below 65 deg C produced a disappearance of order lines and a transition from quadratic gamma ' to cubic gamma . The data are plotted and indicate that a continuous phase charge takes place. (T.R.H.)
- Research Organization:
- Centre d'Etudes Nucleaires, Saclay, France
- NSA Number:
- NSA-14-014100
- OSTI ID:
- 4160680
- Journal Information:
- J. Nuclear Materials, Journal Name: J. Nuclear Materials Vol. Vol: 2
- Country of Publication:
- Country unknown/Code not available
- Language:
- French
Similar Records
STUDY OF DISORDERING BY IRRADIATION OF U$sub 2$Mo
ISOTHERMAL TRANSFORMATION OF U-14 AND U-16 WT % Mo ALLOYS AT 550 C. Interim Report
SELF-DIFFUSION OF URANIUM IN THE /cap beta/ PHASE
Journal Article
·
Tue Feb 28 23:00:00 EST 1961
· J. Nuclear Materials
·
OSTI ID:4043739
ISOTHERMAL TRANSFORMATION OF U-14 AND U-16 WT % Mo ALLOYS AT 550 C. Interim Report
Technical Report
·
Thu Nov 30 23:00:00 EST 1961
·
OSTI ID:4825994
SELF-DIFFUSION OF URANIUM IN THE /cap beta/ PHASE
Journal Article
·
Thu Oct 01 00:00:00 EDT 1959
· J. Nuclear Materials
·
OSTI ID:4221181