Non-classical nucleation theory of ordered intermetallic precipitates -- application to the Al-Li alloy
- Pennsylvania State Univ., University Park, PA (United States). Dept. of Materials Science and Engineering
The continuum non-classical nucleation theory of Cahn and Hilliard for isostructural decomposition has been extended to the case in which the precipitate and matrix not only have different compositions, but also have different structures. The particular example of precipitation of ordered intermetallics from a disordered matrix is considered. It is found that a critical nucleus consists of fluctuations of both composition and long-range order parameter profiles. It is shown that only when the composition of the initial disordered matrix is near the phase boundary of the disordered phase, are the composition and order parameter values inside the critical nucleus close to those of the equilibrium ordered phase, and that the critical profiles become increasingly diffuse as the composition of the disordered matrix approaches the ordering instability line. Based on the non-classical nucleation theory, the size of critical fluctuations, the critical free energy change and the nucleation rate are estimated for the specific case of the precipitation of metastable {delta}{prime} ordered phase from a disordered matrix in the Al-Li alloy.
- OSTI ID:
- 415417
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 10 Vol. 44; ISSN 1359-6454; ISSN ACMAFD
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of crystallography upon critical nucleus shapes and kinetics of homogeneous f. c. c. -f. c. c. nucleation-II. The non-classical regime
Influence of crystallography upon critical nucleus shapes and kinetics of homogeneous f. c. c. -f. c. c. nucleation-IV. Comparisons between theory and experiment in Cu-Co alloys