THE PHASE DIAGRAM FOR THE BINARY SYSTEM CADMIUM-TELLURIUM. Report No. 2900-139-R
Technical Report
·
OSTI ID:4121669
The phase diagram for the Cd -Te system was determined using differential thermal analysis. Thermodynamic analysis showed that the system CdTe-Te appeared to form an ideal solution. The latent heat of fusion of CdTe is estimated to be 16,706 cal/gram molecule. It was found that the system Cd-CdTe is an elementary solution and has a relatively large excess partial molar entropy of solution and a large partial molar enthalpy of solution. These partial molar qualities were independent functions of composition, but not of temperature. The eutectic compositions were determined as 10/sup -6/ atom-fraction tellurium and about 0.99 atom-fraction tellurium. (auth)
- Research Organization:
- Michigan. Univ., Ann Arbor. Willow Run Labs.
- DOE Contract Number:
- DA-36-039 SC-78801
- NSA Number:
- NSA-15-001821
- OSTI ID:
- 4121669
- Report Number(s):
- AD-235831
- Resource Relation:
- Other Information: Project MICHIGAN. Orig. Receipt Date: 31-DEC-61
- Country of Publication:
- United States
- Language:
- English
Similar Records
Partial pressures over the pseudobinary solid solution Hg /SUB 1-x/ Cd /SUB x/ Te(s) for x=0. 70 and 0. 95 and over four Te-rich ternary melts
Chemical vapor deposition of cadmium telluride. Final technical report, 1 Jun 1973--31 Jan 1975
THERMODYNAMIC PROPERTIES OF NONSTOICHIOMETRIC NICKEL TELLURIDES AND OF TELLURIUM (thesis)
Journal Article
·
Mon Apr 01 00:00:00 EST 1985
· J. Electrochem. Soc.; (United States)
·
OSTI ID:4121669
Chemical vapor deposition of cadmium telluride. Final technical report, 1 Jun 1973--31 Jan 1975
Technical Report
·
Sat Mar 01 00:00:00 EDT 1975
·
OSTI ID:4121669
THERMODYNAMIC PROPERTIES OF NONSTOICHIOMETRIC NICKEL TELLURIDES AND OF TELLURIUM (thesis)
Technical Report
·
Tue Jan 01 00:00:00 EST 1957
·
OSTI ID:4121669