Fatigue behavior of carbon fiber reinforced epoxy composites -[{+-}45]{sub 4s} laminate under tension-tension and tension - compression fatigue loading test
Conference
·
OSTI ID:412054
- National Tsing Hua Univ., Hsin-Chu (Taiwan, Province of China); and others
Fatigue behaviors of carbon fiber reinforced epoxy laminated composite have been investigated. The [{+-}45]4S laminates of T300/976 Carbon/Epoxy were utilized. The static tensile strength and tension-tension tension-compression fatigue loading tests at various levels of stress amplitude were measured. The median rank method was applied to predict the statistical probability of experimental data of fatigue life. The S-N curves for various survival probabilities were established using the pooled Weibull distribution function. The theoretical prediction methods could be applied to illustrate the fatigue behavior of thermoset matrix polymer composites. Furthermore, the fatigue behaviors under tension - tension and tension-compression fatigue loading test were investigated. Both the stiffness degradation and the surface temperature change during fatigue test are discussed.
- OSTI ID:
- 412054
- Report Number(s):
- CONF-960310--; CNN: Contract NSC 84-2623-D-007-011
- Country of Publication:
- United States
- Language:
- English
Similar Records
Tension-Compression fatigue behavior of carbon fiber reinforced epoxy quasi-isotropic laminated composites subjected to low energy impact
Fatigue behavior of carbon fiber reinforced polyetheretherketone (PEEK) laminated composites (III)
Mechanical behavior of laminated composites at elevated temperatures
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:412053
Fatigue behavior of carbon fiber reinforced polyetheretherketone (PEEK) laminated composites (III)
Conference
·
Thu Dec 30 23:00:00 EST 1993
·
OSTI ID:143643
Mechanical behavior of laminated composites at elevated temperatures
Thesis/Dissertation
·
Sat Dec 31 23:00:00 EST 1988
·
OSTI ID:7202700