VOID FORMATION IN PROTON-IRRADIATED STAINLESS STEEL.
- Research Organization:
- Atomics International, Canoga Park, Calif.
- DOE Contract Number:
- AT(04-3)-824
- NSA Number:
- NSA-24-036937
- OSTI ID:
- 4119600
- Report Number(s):
- AI-AEC--12961
- Country of Publication:
- United States
- Language:
- English
Similar Records
Atom displacements and void formation in proton-irradiated Type 316 stainless steel
Void formation in cold-worked Type 316 stainless steel irradiated with 1- MeV protons
STUDIES OF VOID FORMATION IN PROTON-IRRADIATED TYPE 316 AND TITANIUM- MODIFIED 316 STAINLESS STEELS.
Technical Report
·
Fri Aug 30 00:00:00 EDT 1974
·
OSTI ID:4282409
Void formation in cold-worked Type 316 stainless steel irradiated with 1- MeV protons
Technical Report
·
Fri Jun 28 00:00:00 EDT 1974
·
OSTI ID:4261985
STUDIES OF VOID FORMATION IN PROTON-IRRADIATED TYPE 316 AND TITANIUM- MODIFIED 316 STAINLESS STEELS.
Technical Report
·
Fri Dec 31 23:00:00 EST 1971
·
OSTI ID:4694494
Related Subjects
ATOMS
BUBBLES
DEFECTS
DISLOCATIONS
EXPANSION
HIGH TEMPERATURE
MEV RANGE
N30150* --Metals
Ceramics
& Other Materials--Metals & Alloys--Radiation Effects
PRODUCTION
PROTONS
PROTONS/effects on void formation in Type 316 stainless steel at 1.2 MeV
STAINLESS STEEL-316
STAINLESS STEEL/radioinduced void formation in Type 316
1.2-MeV proton
STAINLESS STEELS
SWELLING
VOIDS
BUBBLES
DEFECTS
DISLOCATIONS
EXPANSION
HIGH TEMPERATURE
MEV RANGE
N30150* --Metals
Ceramics
& Other Materials--Metals & Alloys--Radiation Effects
PRODUCTION
PROTONS
PROTONS/effects on void formation in Type 316 stainless steel at 1.2 MeV
STAINLESS STEEL-316
STAINLESS STEEL/radioinduced void formation in Type 316
1.2-MeV proton
STAINLESS STEELS
SWELLING
VOIDS