KINETICS OF THE OXIDATION OF A THORIA-10 w/o URANIA SINTERED PELLET
Technical Report
·
OSTI ID:4115214
A thoria-10 wt.% urania sintered pellet was oxidized at temperatures from 600 to 950 deg C and 779 mm Hg oxygen pressure. The rate of oxidation can be expressed as: R = 3.T x 10/sup -3/ e/sup -22//sup ,50//sup 0/R//sup T/ moles O/ sub / 2>i/cm/sup 2/-min from 800 to 95O deg C. The pellet was not pulverized under the experimental conditions. (auth)
- Research Organization:
- Atomics International. Div. of North American Aviation, Inc., Canoga Park, Calif.
- NSA Number:
- NSA-15-007770
- OSTI ID:
- 4115214
- Report Number(s):
- NAA-SR-Memo-5773
- Country of Publication:
- United States
- Language:
- English
Similar Records
THORIA AND THORIA-URANIA REINFORCED BY METAL FIBERS
KINETICS AND MECHANISM OF THE OXIDATION OF URANIUM DIOXIDE AND URANIUM DIOXIDE PLUS FISSIA SINTERED PELLETS
SINTERING OF THORIA GEL. Technical Report No. XXIII
Technical Report
·
Fri Jun 01 00:00:00 EDT 1962
·
OSTI ID:4767924
KINETICS AND MECHANISM OF THE OXIDATION OF URANIUM DIOXIDE AND URANIUM DIOXIDE PLUS FISSIA SINTERED PELLETS
Technical Report
·
Mon Oct 31 23:00:00 EST 1960
·
OSTI ID:4117332
SINTERING OF THORIA GEL. Technical Report No. XXIII
Technical Report
·
Thu Jan 09 23:00:00 EST 1964
·
OSTI ID:4106058