MECHANICAL PROPERTIES OF IRRADIATED WELDS IN STAINLESS STEEL
Technical Report
·
OSTI ID:4072059
Neutron irradiation at a temperature below lOO deg C increased the strength and hardness and decreased the ductility of specimens that had been machined from welded stainless-steel plate. Welds in type 304 stainless steel had a higher yield strength and lower ductility than the parent plate, both before and aiter exposure to 1.2 x lO/sup 21/ fast neutrons/cm 2. The ultimate strengths of weld metal, heataffected zone, and parent plate were apprcximately equal, both before and after irradiation. (auth)
- Research Organization:
- Du Pont de Nemours (E.I.) & Co. Savannah River Lab., Aiken, S.C.
- NSA Number:
- NSA-15-011703
- OSTI ID:
- 4072059
- Report Number(s):
- DP-534
- Country of Publication:
- United States
- Language:
- English
Similar Records
INFLUENCE OF BORON ON PRE- AND POST IRRADIATION PROPERTIES OF TYPE 304 STAINLESS STEEL AND WELD METAL
Low dose irradiation effects on heat-to-heat variation of type 304 stainless steel creep and tensile properties
Tensile properties of irradiated and unirradiated welds of A533 steel plate and A508 forgings
Technical Report
·
Tue Jun 14 00:00:00 EDT 1960
·
OSTI ID:4782071
Low dose irradiation effects on heat-to-heat variation of type 304 stainless steel creep and tensile properties
Conference
·
Thu Dec 31 23:00:00 EST 1981
· Am. Soc. Test. Mater., Spec. Tech. Publ.; (United States)
·
OSTI ID:5709689
Tensile properties of irradiated and unirradiated welds of A533 steel plate and A508 forgings
Technical Report
·
Mon Dec 31 23:00:00 EST 1979
·
OSTI ID:5643630