RUBIDIUM EVALUATION PROGRAM. Quarterly Technical Report No. 6 fof Period May 1 through July 31, 1960
Technical Report
·
OSTI ID:4037748
The first corrosion test capsule run was completed. A type 316 stainless steel capsule containing approximately 12.5 g of Rb was subjected to a boiling-refluxing type static capsule test for 50 hours at 1550 deg F and 50 hours at 1800 F. Very little attack on stainless steel was observed. The final design of the basic corrosion loop was completed. A boiling apparatus will be used for measuring the vapor pressure-temperature equilibria and the latent heat of vaporization for Rb over the temperature range 1000 to 1800 deg F. (W.L.H.)
- Research Organization:
- Aerojet-General Nucleonics, San Ramon, Calif.
- NSA Number:
- NSA-15-015962
- OSTI ID:
- 4037748
- Report Number(s):
- AGN-8016
- Country of Publication:
- United States
- Language:
- English
Similar Records
RUBIDIUM EVALUATION PROGRAM. Quarterly Technical Report No. 3 for Period February 1 through April 30, 1960
SPACE SYSTEMS TECHNOLOGY STUDIES RUBIDIUM EVALUATION PROGRAM. Report No. 9. Quarterly Technical Report, August 1 through October 31, 1960
DESIGN AND OPERATION OF 1800 F PUMPED BOILING RUBIDIUM LOOP SYSTEM AND DETERMINATION OF DENSITY AND VAPOR PRESSURE RUBIDIUM BETWEEN 174 AND 1800 F. Space Power Systems Technology Studies: Rubidium, Corrosion and Physical Properties Evaluation Program. Final Report (Report No. 16), February 1, 1960 through May 31, 1961
Technical Report
·
Sat Apr 30 00:00:00 EDT 1960
·
OSTI ID:4052038
SPACE SYSTEMS TECHNOLOGY STUDIES RUBIDIUM EVALUATION PROGRAM. Report No. 9. Quarterly Technical Report, August 1 through October 31, 1960
Technical Report
·
Mon Oct 30 23:00:00 EST 1961
·
OSTI ID:4079682
DESIGN AND OPERATION OF 1800 F PUMPED BOILING RUBIDIUM LOOP SYSTEM AND DETERMINATION OF DENSITY AND VAPOR PRESSURE RUBIDIUM BETWEEN 174 AND 1800 F. Space Power Systems Technology Studies: Rubidium, Corrosion and Physical Properties Evaluation Program. Final Report (Report No. 16), February 1, 1960 through May 31, 1961
Technical Report
·
Tue Oct 30 23:00:00 EST 1962
·
OSTI ID:4784306