HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS. First Quarterly Progress Report, June 1, 1960 to August 31, 1960
The effect of various dipping times, temperatures, and diffusion treatments was determined for tantalum sheet dipped in aluminum alloy baths. Both aluminide and beryllide coatings were produced that will withstand oxidation for 10 hours at 2500 deg F, isothermally and cyclic. Aluminide coatings were obtained on a stressed niobium alloy that meets the same test conditions. (auth)
- Research Organization:
- Sylvania-Corning Nuclear Corp., Bayside, N.Y.
- NSA Number:
- NSA-15-015995
- OSTI ID:
- 4037374
- Report Number(s):
- SCNC-315
- Country of Publication:
- United States
- Language:
- English
Similar Records
HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS. Second Quarterly Progress Report, September 1, 1960 to November 30, 1960
HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS. Quarterly Progress Report No. 3, Period Covered December 1, 1960-February 28, 1961
HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS
Technical Report
·
Mon Oct 30 23:00:00 EST 1961
·
OSTI ID:4033373
HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS. Quarterly Progress Report No. 3, Period Covered December 1, 1960-February 28, 1961
Technical Report
·
Mon Oct 30 23:00:00 EST 1961
·
OSTI ID:4051085
HIGH TEMPERATURE OXIDATION RESISTANT COATINGS FOR TANTALUM BASE ALLOYS
Technical Report
·
Tue Aug 01 00:00:00 EDT 1961
·
OSTI ID:4836630