Combinatorial fabrication and studies of intense efficient ultraviolet--violet organic light-emitting device arrays
Arrays of ultraviolet--violet (indium tin oxide)/[copper phthalocyanine (CuPc)]/[4,4'-bis(9-carbazolyl)biphenyl (CBP)]/[2-(4-biphenylyl)-5-(4-tert-butylphenyl)-1,3,4oxadiazole (Bu-PBD)]/CsF/Al organic light-emitting devices, fabricated combinatorially using a sliding shutter technique, are described. Comparison of the OLED electroluminescence and CBP photoluminescence spectra indicates that the emission originates from the bulk of that layer. In arrays of devices in which the thickness of the CuPc and Bu--PBD were varied, but that of CBP was fixed at 50 nm, the optimal radiance R was obtained at CuPc and Bu--PBD thicknesses of 15 and 18 nm, respectively. At 10 mA/cm{sup 2}, R was 0.38 mW/cm{sup 2}, i.e., the external quantum efficiency was 1.25%; R increased to {approx}1.2 mW/cm{sup 2} at 100 mA/cm{sup 2}.
- Sponsoring Organization:
- (US)
- DOE Contract Number:
- W-7405-ENG-82
- OSTI ID:
- 40277766
- Journal Information:
- Applied Physics Letters, Journal Name: Applied Physics Letters Journal Issue: 14 Vol. 79; ISSN 0003-6951
- Publisher:
- The American Physical Society
- Country of Publication:
- United States
- Language:
- English
Similar Records
Device Optimization and Transient Electroluminescence Studies of Organic light Emitting Devices
Thin air-plasma-treated alkali fluoride layers for improved hole extraction in copper phthalocyanine/C70-based solar cells
Interfacial energy level bending in a crystalline p/p-type organic heterostructure
Thesis/Dissertation
·
Tue Aug 05 00:00:00 EDT 2003
·
OSTI ID:816439
Thin air-plasma-treated alkali fluoride layers for improved hole extraction in copper phthalocyanine/C70-based solar cells
Journal Article
·
Mon Mar 12 00:00:00 EDT 2012
· Optical Engineering
·
OSTI ID:1060778
Interfacial energy level bending in a crystalline p/p-type organic heterostructure
Journal Article
·
Mon May 16 00:00:00 EDT 2011
· Applied Physics Letters
·
OSTI ID:21518447