Moduli of elasticity of Fe{sub 80}B{sub 12}Si{sub 8} metallic glass strips annealed in vacuum at 370 and 380 C
Journal Article
·
· IEEE Transactions on Magnetics
- Polish Academy of Sciences, Warszawa (Poland). Inst. of Physics
- Naples Univ., Napoli (Italy)
Elasticity moduli at constant magnetic field and at constant induction as the functions of magnetic bias field of the strips of Fe{sub 80}B{sub 12}Si{sub 8} metallic glass annealed in vacuum at temperatures of 370 and 380 C were investigated. The values of moduli in as-quenched state were changing from 133 to 155 GPa. After annealing at 370 C the moduli changes were from 80 to 170 GPa and after heat treatment at 380 C {Delta}E effect increased and these changes were from 60 to 170 CPa.
- OSTI ID:
- 40237
- Report Number(s):
- CONF-930860-; ISSN 0018-9464; TRN: IM9520%%432
- Journal Information:
- IEEE Transactions on Magnetics, Vol. 30, Issue 2Pt2; Conference: EMMA `93: 5th European magnetic materials and applications conference, Kosice (Slovakia), 24-27 Aug 1993; Other Information: PBD: Mar 1994
- Country of Publication:
- United States
- Language:
- English
Similar Records
Post magnetic field annealing effect on magnetic and structural properties of Co{sub 80}Pt{sub 20} nanowires and nanotubes fabricated by electrochemical method
Correlation of magnetic and mechanical properties of hydrogenated, compositionally modulated, amorphous Fe{sub 80}Zr{sub 20} films (abstract)
40% tunneling magnetoresistance after anneal at 380{degree}C for tunnel junctions with iron{endash}oxide interface layers
Journal Article
·
Wed May 07 00:00:00 EDT 2014
· Journal of Applied Physics
·
OSTI ID:40237
+3 more
Correlation of magnetic and mechanical properties of hydrogenated, compositionally modulated, amorphous Fe{sub 80}Zr{sub 20} films (abstract)
Journal Article
·
Mon Apr 01 00:00:00 EST 1996
· Journal of Applied Physics
·
OSTI ID:40237
+2 more
40% tunneling magnetoresistance after anneal at 380{degree}C for tunnel junctions with iron{endash}oxide interface layers
Journal Article
·
Fri Jun 01 00:00:00 EDT 2001
· Journal of Applied Physics
·
OSTI ID:40237
+4 more