MECHANISMS AND KINETICS OF URANIUM CORROSION AND URANIUM CORE FUEL ELEMENT RUPTURES IN WATER AND STEAM
The mechanisms and kinetics of uranium corrosion and fuel element ruptures were investigated in water and steam at 170 to 500 deg C and at 100 to 2800 psig. The fuel element samples were coextruded Zircaloy-clad uranium-core rods and tubes which were defected prior to exposure. Uranium corrosion was found to be the sum of two processes; direct oxidation by water, and oxidation of uranium hydride intermediate. Fuel element ruptures occur in two stages; an initial induction period followed by an accelerating corrosion of the core causing the cladding to blister, swell, and fracture. Uranium corrosion and fuel element ruptures were examined with respect to temperature, pressure, steam versus liquid water, heat treatment, carbon content of uranium, zirconium content of uranium, cladding thickness, fuel geometry, annular spacings, defect geometry and size, coolant flow, hydriding of Zircaloy components, and irradiation effects. (auth)
- Research Organization:
- General Electric Co. Hanford Atomic Products Operation, Richland, Wash.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AT(45-1)-1350
- NSA Number:
- NSA-15-017253
- OSTI ID:
- 4023654
- Report Number(s):
- HW-67370
- Country of Publication:
- United States
- Language:
- English
Similar Records
Irradiation performance of enriched seven-rod cluster fuel elements with 20- and 30-mil-thick cladding, Supplement B to production test IP-226-A, (RM-562): Final report
RUPTURE KINETICS OF ZIRCALOY-CLAD FUEL ELEMENTS IN HIGH TEMPERATURE WATER AND STEAM. Interim Report No. 6. Effects of Carbon and Zirconium Content on Uranium Corrosion and Rupture Mechanisms
RUPTURE KINETICS OF ZIRCALOY CLAD FUEL ELEMENTS IN HIGH TEMPERATURE WATER AND STEAM. CO-EXTRUDED ROD ELEMENTS WITH PINHOLE DEFECTS. Interim Report No. 2
Technical Report
·
Sun Jul 01 00:00:00 EDT 1962
·
OSTI ID:10169384
RUPTURE KINETICS OF ZIRCALOY-CLAD FUEL ELEMENTS IN HIGH TEMPERATURE WATER AND STEAM. Interim Report No. 6. Effects of Carbon and Zirconium Content on Uranium Corrosion and Rupture Mechanisms
Technical Report
·
Tue Dec 29 23:00:00 EST 1959
·
OSTI ID:4814722
RUPTURE KINETICS OF ZIRCALOY CLAD FUEL ELEMENTS IN HIGH TEMPERATURE WATER AND STEAM. CO-EXTRUDED ROD ELEMENTS WITH PINHOLE DEFECTS. Interim Report No. 2
Technical Report
·
Sat Aug 01 00:00:00 EDT 1959
·
OSTI ID:4702030